| 拉伸模量 | --- | ASTM D-638 | 2410 | MPa |
| 弯曲强度 | --- | ASTM D-790 | 96 | MPa |
| 弯曲模量 | --- | ASTM D-790 | 2410 | MPa |
| 缺口冲击强度 | 23℃ | ASTM D-256 | 900 | J/m |
| 冲击强度 | 23℃ | ASTM D-256 | 未破裂 | --- |
| 落锤冲击强度 | 总能量@23℃ | ASTM D-3763 | 87 | J |
| 洛氏硬度 | --- | ASTM D-785 | 73 | M标度 |
| 电气性能 | 辉光灯丝测试 | 2mm | IEC 695-2-1 | 850 | ℃ |
| 对比电弧径迹指数 | 2mm | IEC 112 | 250 | V |
| 介电强度 | 60Hz | ASTM D-149 | 17 | kv/mm |
| 损耗因素 | 60Hz | ASTM D-150 | 0.001 | --- |
| 体积电阻率 | 23℃，干 | ASTM D-257 | 2.0×1017 | Ω.cm |
| 热 性 能 | 平均燃烧程度 | --- | ASTM D-635 | 25 | mm |
| 球状压痕温度 | --- | IEC 598-1 | >125 | ℃ |
| 维卡软化点 | 50℃/hour | ASTM D-1525 | 149 | ℃ |
| 线性热收缩率 | @-40℃-82℃ | ASTM D-785 | 68×10-6 | mm/mm/℃ |
| 热变形温度 | 退火@0.45MPa(4mm) | ASTM D-648 | 144 | ℃ |
| 热变形温度 | 退火@1.82MPa(4mm) | ASTM
D-648 |