Q420，是一种低合金高强度结构钢
【化学成分】（质量分数）（%）
| 等级 | C | Mn | Si | P | S | V | Nb | Ti | Al | Cr | Ni |
| A | ≦0.20 | 1.00～1.70 | ≦0.55 | ≦0.045 | ≦0.045 | 0.02～0.20 | 0.015～0.060 | 0.02～0.20 | - | ≦0.40 | ≦0.70 |
| B | ≦0.20 | 1.00～1.70 | ≦0.55 | ≦0.040 | ≦0.040 | 0.02～0.20 | 0.015～0.060 | 0.02～0.20 | - | ≦0.40 | ≦0.70 |
| C | ≦0.20 | 1.00～1.70 | ≦0.55 | ≦0.035 | ≦0.035 | 0.02～0.20 | 0.015～0.060 | 0.02～0.20 | ≧0.015 | ≦0.40 | ≦0.70 |
| D | ≦0.20 | 1.00～1.70 | ≦0.55 | ≦0.030 | ≦0.030 | 0.02～0.20 | 0.015～0.060 | 0.02～0.20 | ≧0.015 | ≦0.40 | ≦0.70 |
| E | ≦0.20 | 1.00～1.70 | ≦0.55 | ≦0.025 | ≦0.025 | 0.02～0.20 | 0.015～0.060 | 0.02～0.20 | ≧0.015 | ≦0.40 | ≦0.70 |
【抗拉强度】（σb/MPa）
520～680
【伸长率】（δ5/%）
| 等级 | δ5/% |
| A | ≧18 |
| B | ≧18 |
| C | ≧19 |
| D | ≧19 |
| E | ≧19 |
【屈服点】（σs/MPa）
| 厚度（直径、边长）/mm | ≦16 | >16～35 | >35～50 | >50～100 |
| σs/MPa | ≧420 | ≧400 | ≧380 | ≧360 |
【冲击吸收功】（Akv（纵向）/J）
| 等级￤温度 | +20℃ | 0℃ | -20℃ | -40℃ |
| A | | | | |
| B | ≧34 | | | |
| C | | ≧34 | | |
| D | | | ≧34 | |
| E | | | | ≧27 |
【主要特性】
Q420具有高的强度，良好的抗疲劳性能；高韧性和低的脆性转变温度；良好的冷成型性能和焊接性能；具有较好的搞腐蚀性能和一定的耐磨性能。强度高，特别是在正火或正火加回火状态有较高的综合力学性能。
【应用举例】
大型船舶、桥梁、电站设备、中高压锅炉、高压容器、机车车辆、超重机械、矿山机械、及其他大型焊接结构件