CMoV模具钢的淬透性、淬火回火的硬度、耐磨性、强度均比C高。用于制造截面较大、形状复杂、工作条件繁重下的各种冷冲模具和工具，如冲孔凹模、切边模、滚边模、钢板CMov厚板深拉伸模、圆锯、标准工具和量规、螺纹滚模等。

  碳 C ：1.45～1.70

   硅 Si：≤0.40

  锰 Mn：≤0.40

  硫 S ：≤0.030

  磷 P ：≤0.030

  铬 Cr：11.00～12.50

  镍 Ni：允许残余含量≤0.25

  铜 Cu：允许残余含量≤0.30

  钒 V ：0.15～0.30

  钼 Mo：0.40～0.60

  退火,255～207HB,压痕直径3.8～4.2mm;淬火,≥58HRC

  CMoV模具钢淬透性、淬火回火后的硬度、强度、韧性比CR12高，直径为300~400mm以下的工作可完全淬透，淬火变形小，但高温塑性较差。CMoV多用于制造截面较大、形状复杂、工作负荷较重的合种模具和工具。