供应PPS 雪佛龙菲利普斯 BR111 加矿纤玻纤 高强度本色 阻燃VO
'
Ryton® BR111 and BR111BL PPS are glass and mineral filled polyphenylene sulfide compounds developed to provide a good combination of mechanical strength and electrical properties. |
材料状态 | |
资料 1 | - Processing - Injection Molding (English)
- Processing - Machining (English)
| - Processing - Ryton & Xtel Process Comparison (English)
- Processing - Ryton (English)
| - Technical Datasheet (English)
|
|
UL 黄卡 2 | |
搜索 UL 黄卡 | - Chevron Phillips Chemical Company LLC
|
供货地区 | |
填料/增强材料 | |
性能特点 | |
RoHS 合规性 | |
外观 | |
形式 | |
加工方法 | |
比重 | 1.94 | g/cm³ | ASTM D792 |
收缩率 | | | No Standard |
流动:
3.18 mm | 0.20 | % | |
横向流动:
3.18 mm | 0.50 | % | |
吸水率 (23°C, 24 hr) | 0.020 | % | ASTM D570 |
拉伸应力 | | | |
屈服 | 165 | MPa | ISO 527-2 |
-- | 159 | MPa | ASTM D638 |
伸长率 (断裂) | 1.1 | % | ASTM D638, ISO 527-2 |
弯曲模量 | | | |
-- | 19300 | MPa | ASTM D790 |
-- | 19000 | MPa | ISO 178 |
弯曲强度 | | | |
-- | 248 | MPa | ASTM D790 |
-- | 250 | MPa | ISO 178 |
压缩强度 | 295 | MPa | ASTM D695 |
悬壁梁缺口冲击强度 | | | |
3.18 mm | 75 | J/m | ASTM D256 |
-- | 7.5 | kJ/m² | ISO 180/A |
无缺口悬臂梁冲击 | | | |
3.18 mm | 320 | J/m | ASTM D256 |
-- | 24 | kJ/m² | ISO 180 |
热变形温度 (1.8 MPa, 退火) | > 260 | °C | ASTM D648 |
'