供应生物降解塑料PLA 美国NatureWorks 4032D 原材料
材料状态 | |
资料 1 | - Processing - BOPP Film (English)
| - Processing - Sheet Extrusion (English)
| - Technical Datasheet (English)
|
|
供货地区 | |
性能特点 | |
用途 | |
机构评级 | |
形式 | |
加工方法 | |
薄膜厚度 - 经测试 | 25 | µm | |
割线模量 | | | ASTM D882 |
MD: 25 µm | 3450 | MPa | |
TD: 25 µm | 3790 | MPa | |
抗张强度 | | | ASTM D882 |
MD: 屈服, 25 µm | 103 | MPa | |
TD: 屈服, 25 µm | 145 | MPa | |
伸长率 | | | ASTM D882 |
MD: 断裂, 25 µm | 180 | % | |
TD: 断裂, 25 µm | 100 | % | |
埃尔曼多夫抗撕强度 | | | ASTM D1922 |
MD: 25 µm | 17 | g | |
TD: 25 µm | 14 | g | |
透氧率 | 550 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
水气透过率 | 330 | g·mm/m²/atm/24 hr | ASTM F1249 |
玻璃转化温度(DSC) | 57.8 | °C | DSC |
熔融温度 | 160 | °C | |
光泽度 (20°, 25.4 µm) | 90 | | ASTM D2457 |
雾度 (25.4 µm) | 2.1 | % | ASTM D1003 |
Spencer Impact: 2.5 joules
Carbon Dioxide transmission rate, ASTM D1434: 3000 cc-mil/m²/24 hr atm
The value listed as Oxygen Permeability, ASTM D3985, was tested in accordance with ASTM D1434 |
干燥温度 | 79.4 | °C | |
干燥时间 | 4.0 | hr | |
建议的最大水分含量 | 0.025 | % | |
第1气缸区温度 | 179 | °C | |
第2气缸区温度 | 191 | °C | |
第3气缸区温度 | 199 | °C | |
连接器温度 | 199 | °C | |
熔体温度 | 202 到 218 | °C | |
模具温度 | 199 | °C |