ABS XR-404高耐热性韩国LG
'
ABS XR-404产品物性：
比重 | 1.05 | g/cm³ | ASTM D792 |
熔流率 (220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
收缩率 - 流动 (3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
Dimensional Stability | 0.0 | % | ASTM D1042 |
洛氏硬度 (R 计秤) | 108 | | ASTM D785 |
抗张强度 3 (屈服, 3.20 mm) | 48.1 | MPa | ASTM D638 |
伸长率 3 (断裂, 3.20 mm) | 25 | % | ASTM D638 |
弯曲模量 4 (3.20 mm) | 2550 | MPa | ASTM D790 |
弯曲强度 4 (3.20 mm) | 77.5 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 | | | ASTM D256 |
-30°C, 3.20 mm | 69 | J/m | |
-30°C, 6.40 mm | 59 | J/m | |
23°C, 3.20 mm | 220 | J/m | |
23°C, 6.40 mm | 200 | J/m | |
热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火, 6.40 mm | 108 | °C | |
1.8 MPa, 未退火, 6.40 mm | 100 | °C | |
维卡软化温度 | 108 | °C | ASTM D1525 5 |
RTI Elec | | | UL 746 |
1.50 mm | 60.0 | °C | |
3.00 mm | 60.0 | °C | |
RTI Imp | | | UL 746 |
1.50 mm | 60.0 | °C | |
3.00 mm | 60.0 | °C | |
RTI Str | | | UL 746 |
1.50 mm | 60.0 | °C | |
3.00 mm | 60.0 | °C |
'