PA66/美国杜邦/70G13HS1-L热稳定性,高强度,增强级,耐高温PA66
'
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 吸水率 | 饱和(23℃) | ASTM D-570 | 7.1 | % |
| 比重 | | ASTM D-792 | 1.22 |
| 断裂伸长率 | 23℃,DAM | ASTM D-638 | 2 | % |
| 拉伸强度 | 23℃,DAM | ASTM D-638 | 103.4 | MPa |
| 拉伸强度 | 23℃,50%RH | ASTM D-638 | 82.7 | MPa |
| 埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 53 | j/m |
| 挠曲强度 | 23℃,DAM | ASTM D-790 | 165 | MPa |
| 挠曲模量 | 23℃,DAM | ASTM D-790 | 4826 | MPa |
| 洛氏硬度R | DAM | ASTM D-785 | R122 |
| 挤剪强度 | 23℃,DAM | ASTM D-732 | 76 | MPa |
| 洛氏硬度M | DAM | ASTM D-785 | M95 |
| 断裂伸长率 | 23℃,50%RH | ASTM D-638 | 8 | % |
| 埃佐冲击强度 | 23℃,DAM | ASTM D-256 | 48 | j/m |
| 挠曲模量 | 23℃,50%RH | ASTM D-790 | 2758 | MPa |
| 洛氏硬度M | 50%RH | ASTM D-785 | M84 |
| 泰伯磨耗量 | 50%RH | | 12 | cycles |
| 洛氏硬度R | 50%RH | ASTM D-785 | R113 |
| 线性热膨胀系数 | | ASTM D-696 | 2.710-5 | m/m/℃ |
| 热畸变温度 | 1.8MPa | ASTM D-648 | 243 | ℃ |
| 熔点 | 50%RH | ASTM D-789 | 255 | ℃ |
| 熔点 | DAM | ASTM D-789 | 255 | ℃ |
'