ABS/韩国锦湖/750SH
'
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 阻燃性 | | UL-94 | HB | |
| 熔体流动速率 | 200℃ 5kg | ASTM D-1238 | 4.5 | g/10min |
| 模塑收缩率 | | ASTM D-955 | 0.4-0.7 | % |
| 比重 | | ASTM D-792 | 1.04 | 23/23℃ |
| 熔体流动速率 | 200℃ 21.6kg | 锦湖方法 | 50 | g/10min |
| 机械性能 | 弯曲模量 | 23℃ | ASTM D-790 | 24000(340000) | kg/cm2(psi) |
| IZOD冲击强度 | 1/8in(3.2mm) 23℃ | ASTM D-256 | 26(4.7) | kg.cm/cm(ft.ld/in) |
| 洛氏硬度 | | ASTM D-785 | 108 | R |
| 伸长率 | | ASTM D-638 | 30 | % |
| 拉伸强度 | 23℃ | ASTM D-638 | 480(6800) | kg/cm2(psi) |
| 弯曲强度 | 23℃ | ASTM D-790 | 650(9300) | kg/cm2(psi) |
| IZOD冲击强度 | 1/4in(6.4mm) 23℃ | ASTM D-256 | 23(4.2) | kg.cm/cm(ft.ld/in) |
| 热性能 | 热变形温度 | 未退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 85(185) | ℃(℉) |
| 退火 | 6.4mm 18.6kg/cm2 | ASTM D-648 | 95(203) | ℃(℉) |
| 维卡软化点 | | ASTM D-1525 | 95(203) | ℃(℉) |
| 其它性能 | 食品卫生性 | | | 适合 | |
'