产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 密度 | | ASTM D-792 | 1200 | kg/m3 |
| 平衡吸水率 | 23℃，相对湿度50% | ASTM D-570 | 0.32 | % |
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.15 | % |
| 熔体流动速率 | 300℃/1.2kg | ASTM D-1238 | 8 | g/10min |
| 物理性能 | 透光率 | | ASTM D-1003 | 89 | % |
| 模具收缩率 | | ASTM D-955 | 0.005-0.007 | mm/mm |
| 雾度 | | ASTM D-1003 | 0.7-1.5 | % |
| 折射率 | | ASTM D-542 | 1.586 | |
| 机械性能 | 洛氏硬度 | | ASTM D-785 | 73 | M标度 |
| 落锤冲击强度 | 总能量@23℃ | ASTM D-3763 | 89 | J |
| 弯曲模量 | | ASTM D-790 | 2410 | MPa |
| 拉伸模量 | | ASTM D-638 | 2410 | MPa |
| 冲击强度 | 23℃ | ASTM D-256 | 未破裂 | |
| 弯曲强度 | | ASTM D-790 | 96 | MPa |
| 拉伸强度 | 屈服点 | | ASTM D-638 | 60 | MPa |
| 断裂点 | | ASTM D-638 | 72 | MPa |
| 缺口冲击强度 | 23℃ | ASTM D-256 | 900 | J/m |
| 伸长率 | 屈服点 | | ASTM D-638 | 6 | % |
| 断裂点 | | ASTM D-638 | 150 | % |
| 电气性能 | 体积电阻率 | 23℃，干 | ASTM D-257 | 2.0×1017 | Ω.cm |
| 损耗因素 | 60Hz | ASTM D-150 | 0.001 | |
| 介电强度 | 60Hz | ASTM D-149 | 17 | kv/mm |
| 对比电弧径迹指数 | 2mm | IEC 112 | 250 | V |
| 热性能 | 球状压痕温度 | | IEC 598-1 | >125 | ℃ |
| 维卡软化点 | | ASTM D-1525 | 149 | ℃ |
| 辉光灯丝测试 | 2mm | IEC 695-2-1 | 850 | ℃ |
| 热变形温度 | 未退火@1.82MPa(4mm) | ASTM D-648 | 129 | ℃ |
| 热变形温度 | 退火@1.82MPa(4mm) | ASTM D-648 | 142 | ℃ |
| 热变形温度 | 退火@0.45MPa(4mm) | ASTM D-648 | 145 | ℃ |
| 线性热收缩率 | -40℃～82℃ | ASTM D-696 | 68×10-6 | mm/mm/℃ |
| 其它性能 | 平均燃烧程度 | | ASTM D-635 | 25 | mm |
| 需氧系数 | | ASTM D-2863 | 26 | % |
适用于
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物，根据酯基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。其中由于脂肪族和脂肪族-芳香族聚碳酸酯的机械性能较低，从而限制了其在工程塑料方面的应用。目前仅有芳香族聚碳酸酯获的了工业化生产。由于聚碳酸酯结构上的特殊性，现已成为五大工程塑料中增长速度最快的通用工程塑料。