产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM D792 | 1.20 | g/cm3 |
| | 熔体流动速率 | 300℃/1.2kg | ASTM D1238 | 10 | g/10min |
| | 成型收缩率 | 流动 | ASTM D955 | 0.50-0.70 | % |
| | 吸水率 | 24hr,23℃ | ASTM D570 | 0.20 | % |
| | 洛氏硬度 | R计秤 | ASTM D785 | 120 | |
| 机械性能 | 拉伸强度 | | ASTM D638 | 62.7 | MPa |
| | 伸长率 | 断裂 | ASTM D638 | 110 | % |
| | 弯曲模量 | | ASTM D790 | 2280 | MPa |
| | 弯曲强度 | | ASTM D790 | 90.3 | MPa |
| | 悬壁梁缺口冲击强度 | 3.18mm | ASTM D256 | 881 | J/m |
| 热性能 | 热变形温度 | 0.45MPa,未退火 | ASTM D648 | 135 | ℃ |
| | | 1.8MPa,未退火 | ASTM D648 | 125 | ℃ |
| | 线形膨胀系数 | 流动(40到100℃) | | 0.000060-0.000080 | cm/cm/℃ |
| 电气性能 | 介电常数 | 10MHz | ASTM D150 | 2.90 | |
| | 耗散因数 | 10MHz | ASTM D150 | 0.0090 | |
| | 耐电弧性 | | ASTM D495 | 110 | sec |
| 可燃性 | UL阻燃等级 | 2.60mm | UL94 | HB | |
| | | 2.70mm | UL94 | HB | |
| | | 1.60mm | UL94 | V-2 | |
| | | 1.70mm | UL94 | V-2 | |
| 光学性能 | 透射率 | 3000μm | ASTM D1003 | 89.0 | % |
| | 混浊 | 3000μm | ASTM D1003 | <0.80 | % |
原料用途及物性
适用于
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物，根据酯基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。其中由于脂肪族和脂肪族-芳香族聚碳酸酯的机械性能较低，从而限制了其在工程塑料方面的应用。目前仅有芳香族聚碳酸酯获的了工业化生产。由于聚碳酸酯结构上的特殊性，现已成为五大工程塑料中增长速度最快的通用工程塑料。