现货供应 透明TPX塑胶原料 日本三井 DX845
'
密度 | 0.833 | g/cm³ | ASTM D1505 |
熔流率 (260°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
Spiral Flow 2 | 50.0 | cm | Internal Method |
收缩率 3 | | | Internal Method |
流动 | 1.5 | % | |
横向流动 | 1.2 | % | |
吸水率 (24 hr) | < 0.010 | % | ASTM D570 |
洛氏硬度 (R 计秤) | 87 | | ASTM D785 |
拉伸模量 (23°C) | 1900 | MPa | ASTM D638 |
抗张强度 | | | ASTM D638 |
屈服, 23°C | 30.0 | MPa | |
断裂, 23°C | 25.0 | MPa | |
伸长率 (断裂, 23°C) | 12 | % | ASTM D638 |
弯曲模量 (23°C) | 1600 | MPa | ASTM D790 |
弯曲强度 (23°C) | 47.0 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 (23°C) | 20 | J/m | ASTM D256 |
无缺口伊佐德冲击强度 (23°C) | 10 | kJ/m² | ASTM D256 |
热变形温度 (0.45 MPa, 未退火) | 127 | °C | ASTM D648 |
维卡软化温度 | 174 | °C | ASTM D1525 |
熔融温度 | 233 | °C | DSC |
线形膨胀系数 - 流动 | 0.00012 | cm/cm/°C | ASTM D696 |
体积电阻率 | 1.0E+16 | ohm·cm | ASTM D257 |
介电强度 | 66 | kV/mm | ASTM D149 |
介电常数 | 2.10 | | ASTM D150 |
折射率 | 1.460 | | ASTM D542 |
透射率 | 94.0 | % | ASTM D1003 |
雾度 | 1.1 | % | ASTM D1003 |
'