产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 3.0 | g/10min |
| 比重 | ASTM D-7921.04g/cm3 |
| 模具收缩率 | ASTM D-9550.40-0.70% |
| 拉伸强度 | ASTM D-63833.8MPa |
| 断裂伸长率 | ASTM D-63855% |
| 弯曲模量 | ASTM D-7902070MPa |
| 弯曲强度 | ASTM D-79060.0MPa |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 107 | J/m |
| 热变形温度 | 1.80MPa,未退火 | ASTM D-648 | 75.0 | ℃ |
| 热变形温度 | 1.80MPa,退火 | ASTM D-648 | 98.9 | ℃ |
| 维卡软化温度 | ASTM D-1525106℃ |
| CLTE | Flow | ASTM D-696 | 0.000076 | cm/cm/℃ |
| 阻燃性 | 1.50mm | UL 94 | HB |
| 光泽度 | 60℃ | ASTM D-523 | 92 |
'