挤出级ABS/LG化学/MU620 可注塑挤出成型
ABS LGMU620 挤出成型
比重 | 1.04 | g/cm³ | ASTM D792 |
熔流率(220°C/10.0 kg) | 25 | g/10 min | ASTM D1238 |
收缩率 - 流动(3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
洛氏硬度(R 计秤) | 104 | | ASTM D785 |
抗张强度 2(屈服, 3.20 mm) | 37.3 | MPa | ASTM D638 |
伸长率 2 | | | ASTM D638 |
屈服, 3.20 mm | > 5.0 | % | |
断裂, 3.20 mm | 25 | % | |
弯曲模量 3(3.20 mm) | 2550 | MPa | ASTM D790 |
弯曲强度 3(屈服, 3.20 mm) | 68.6 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 | | | ASTM D256 |
23°C, 3.20 mm | 350 | J/m | |
23°C, 6.40 mm | 310 | J/m | |
热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火, 6.40 mm 4 | 91.0 | °C | |
0.45 MPa, 未退火, 6.40 mm 5 | 84.0 | °C | |
维卡软化温度 | 92.0 | °C | ASTM D1525 6 |