ABS/LG化学/XR-409P
'
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔融指数 | 220℃/10kg | ASTM D-1238 | 3.0 | g/10min |
| 物理性能 | 比重 | | ASTM D-792 | 1.05 | |
| 模具收缩率 | | ASTM D-955 | 0.4-0.7 | % |
| 机械性能 | 拉伸强度 | 50mm/min | ASTM D-638 | 420 | kg/cm2 |
| 伸长率 | 50mm/min | ASTM D-638 | 20 | % |
| 抗弯强度 | 15mm/min | ASTM D-790 | 720 | kg/cm2 |
| 抗弯模数 | 15mm/min | ASTM D-790 | 21000 | kg/cm2 |
| IZOD缺口冲击强度 | Notched 1/4" | ASTM D-256 | 20 | kg.cm/cm |
| IZOD缺口冲击强度 | Notched 1/8" | ASTM D-256 | 23 | kg.cm/cm |
| 洛氏硬度 | | ASTM D-785 | 100 | R-scale |
| 热性能 | 热变形温度 | 18.5kg/cm21/2" | ASTM D-648 | 111 | ℃ |
| 维卡软化点 | 1000g | ASTM D-1525 | 128 | ℃ |
| 阻燃等级 | 1/8" | UL94 | HB | |
| 阻燃等级 | 1/16" | UL94 | HB | |
'