供应 高抗冲PETG JN200 透明PETG原料 韩国SK
'
比重 | 1.23 | g/cm³ | ASTM D792 |
收缩率 - 流动 | 0.20 到 0.50 | % | ASTM D955 |
吸水率 (24 hr) | 0.13 | % | ASTM D570 |
洛氏硬度 (R 计秤) | 105 | | ASTM D785 |
抗张强度 3 | | | ASTM D638 |
屈服 | 45.0 | MPa | |
断裂 | 53.0 | MPa | |
伸长率 3 | | | ASTM D638 |
屈服 | 5.0 | % | |
断裂 | 340 | % | |
弯曲模量 4 | 1800 | MPa | ASTM D790 |
弯曲强度 4 | 67.0 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 (23°C) | 无断裂 | | ASTM D256 |
热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火 | 74.0 | °C | |
1.8 MPa, 未退火 | 64.0 | °C | |
维卡软化温度 | 88.0 | °C | ASTM D1525 5 |
表面电阻率 | 1.0E+16 | ohm | ASTM D257 |
体积电阻率 | 1.0E+15 | ohm·cm | ASTM D257 |
介电常数 | | | ASTM D150 |
1 kHz | 2.80 | | |
1 MHz | 2.60 | | |
耗散因数 | | | ASTM D150 |
1 kHz | 0.0060 | | |
1 MHz | 0.019 | | |
UL 阻燃等级 (3.00 mm) | HB | | UL 94 |
透射率 | 91.0 | % | ASTM D1003 |
雾度 | < 1.0 | % | ASTM D1003 |
'