ASA/沙伯基础(原GE)/CR4020
'
产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
基本性能 | 熔体流动速率 | 220℃/10.0kg | ASTM D-1238 | 7.0 | g/10min |
物理性能 | 比重 | | ASTM D-792 | 1.07 | g/cm3 |
模具收缩率 | Flow,3.20mm | ASTM D-955 | 0.50-0.70 | % |
机械性能 | 拉伸模量 | | ASTM D-638 | 2070 | MPa |
拉伸屈服强度 | | ASTM D-638 | 41.4 | MPa |
拉伸断裂强度 | | ASTM D-638 | 31.7 | MPa |
拉伸屈服伸长率 | | ASTM D-638 | 3.0 | % |
拉伸断裂伸长率 | | ASTM D-638 | 24 | % |
弯曲模量 | 50.0mm Span | ASTM D-790 | 2070 | MPa |
弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 62.1 | MPa |
IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 288 | J/m |
洛氏硬度 | | ASTM D-785 | 95 | R scale |
热性能 | 热变形温度 | 0.45MPa,未退火,3.20mm | ASTM D-648 | 87.8 | ℃ |
热变形温度 | 1.80MPa,未退火,3.20mm | ASTM D-648 | 78.9 | ℃ |
维卡软化温度 | | ASTM D-1525 | 99.4 | ℃ |
CLTE | Flow,-40TO40℃ | ASTM E-831 | 8.6 | cm/cm/℃ |
CLTE | Transverse,-40TO40℃ | ASTM E-831 | 9.2 | cm/cm/℃ |
'