长期代理 低翘曲 高耐化学性PCTG 韩国sk JN-200 透明高抗冲颗粒
'
比重 | 1.23 | g/cm³ | ASTM D792 |
收缩率 - 流动 | 0.20 到 0.50 | % | ASTM D955 |
吸水率(24 hr) | 0.13 | % | ASTM D570 |
洛氏硬度(R 计秤) | 105 | | ASTM D785 |
抗张强度3 | | | ASTM D638 |
屈服 | 45.0 | MPa | |
断裂 | 53.0 | MPa | |
伸长率3 | | | ASTM D638 |
屈服 | 5.0 | % | |
断裂 | 340 | % | |
弯曲模量4 | 1800 | MPa | ASTM D790 |
弯曲强度4 | 67.0 | MPa | ASTM D790 |
悬壁梁缺口冲击强度(23°C) | 无断裂 | | ASTM D256 |
热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火 | 74.0 | °C | |
1.8 MPa, 未退火 | 64.0 | °C | |
维卡软化温度 | 88.0 | °C | ASTM D15255 |
表面电阻率 | 1.0E+16 | ohm | ASTM D257 |
体积电阻率 | 1.0E+15 | ohm·cm | ASTM D257 |
介电常数 | | | ASTM D150 |
1 kHz | 2.80 | | |
1 MHz | 2.60 | | |
耗散因数 | | | ASTM D150 |
1 kHz | 0.0060 | | |
1 MHz | 0.019 | | |
UL 阻燃等级(3.00 mm) | HB | | UL 94 |
透射率 | 91.0 | % | ASTM D1003 |
雾度 | <
1.0 | % | ASTM D1003 |
干燥温度 | 65.0 | °C | |
干燥时间 | 6.0 到 12 | hr | |
建议的最大水分含量 | 0.050 | % | |
螺筒后部温度 | 210 | °C | |
螺筒中部温度 | 245 | °C | |
螺筒前部温度 | 245 | °C | |
射嘴温度 | 245 | °C | |
模具温度 | 40.0 | °C | |
注射速度 | 中等偏慢 | | |
背压 | 0.300 到
1.00 | MPa | |
螺杆转速 | 50 到 100 | rpm |
'