| 产品说明 | |
PPE+PS blend. Unfilled. NSF listed for potable water use in several colors (Standard 61). FDA compliant in several colors (restrictions apply). UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications: valve components, water pump housings, etc. This grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HN731A. |
性能特点 |
| |||
用途 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
比重 | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
熔流率 (280°C/5.0 kg) | 9.2 | g/10 min | ASTM D1238 |
溶化体积流率（MVR） (280°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
收缩率 | Internal Method | ||
流动 : | 0.50 到 0.70 | % | |
横向流动 : | 0.50 到 0.70 | % | |
吸水率 | |||
24 hr | 0.060 | % | ASTM D570 |
饱和, 23°C | 0.23 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.060 | % | ISO 62 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
洛氏硬度 (R 计秤) | 119 |
| ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | |||
-- 3 | 2860 | MPa | ASTM D638 |
-- | 2700 | MPa | ISO 527-2/1 |
抗张强度 | |||
屈服 4 | 58.6 | MPa | ASTM D638 |
屈服 | 57.0 | MPa | ISO 527-2/50 |
断裂 4 | 49.6 | MPa | ASTM D638 |
断裂 | 51.0 | MPa | ISO 527-2/50 |
伸长率 | |||
屈服 4 | 7.2 | % | ASTM D638 |
屈服 | 3.5 | % | ISO 527-2/50 |
断裂 4 | 28 | % | ASTM D638 |
断裂 | 17 | % | ISO 527-2/50 |
弯曲模量 | |||
100 mm 跨距 5 | 2420 | MPa | ASTM D790 |
50.0 mm 跨距 6 | 2650 | MPa | ASTM D790 |
-- 7 | 2550 | MPa | ISO 178 |
弯曲强度 | |||
-- 7, 8 | 95.0 | MPa | ISO 178 |
屈服, 50.0 mm 跨距 6 | 90.3 | MPa | ASTM D790 |
屈服, 100 mm 跨距 5 | 89.6 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度 9 (23°C) | 17 | kJ/m² | ISO 179/1eA |
悬壁梁缺口冲击强度 | |||
-40°C | 130 | J/m | ASTM D256 |
23°C | 210 | J/m | ASTM D256 |
-30°C 10 | 5.0 | kJ/m² | ISO 180/1A |
23°C 10 | 17 | kJ/m² | ISO 180/1A |
装有测量仪表的落镖冲击 (23°C, Total Energy) | 48.8 | J | ASTM D3763 |
落锤冲击 | ASTM D3029 | ||
-40°C | 5.42 | J | |
-30°C | 25.8 | J |
| 热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 | |||
0.45 MPa, 未退火, | 132 | °C | ASTM D648 |
0.45 MPa, 未退火, | 137 | °C | ASTM D648 |
1.8 MPa, 未退火, | 118 | °C | ASTM D648 |
1.8 MPa, 未退火, | 127 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 11 | 120 | °C | ISO 75-2/Af |
维卡软化温度 | |||
-- | 149 | °C | ASTM D1525 12 |
-- | 140 | °C | ISO 306/B50 |
-- | 143 | °C | ISO 306/B120 |
线形膨胀系数 | ASTM E831, ISO 11359-2 | ||
流动 : -40 到 40°C | 0.000092 | cm/cm/°C | |
横向 : -40 到 40°C | 0.000095 | cm/cm/°C | |
RTI Elec | 105 | °C | UL 746 |
RTI Imp | 90.0 | °C | UL 746 |
RTI Str | 105 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
介电强度 (3.20 mm, in Oil) | 22 | kV/mm | ASTM D149 |
介电常数 | ASTM D150 | ||
50 Hz | 2.65 |
| |
60 Hz | 2.65 |
| |
耗散因数 | ASTM D150 | ||
50 Hz | 0.00040 |
| |
60 Hz | 0.00040 |
| |
耐电弧性 13 | PLC 7 |
| ASTM D495 |
相比耐漏电起痕指数(CTI) | PLC 3 |
| UL 746 |
高电弧燃烧指数(HAI) | PLC 0 |
| UL 746 |
高电压电弧起痕速率 (HVTR) | PLC 4 |
| UL 746 |
热丝引燃 (HWI) | PLC 2 |
| UL 746 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
UL 阻燃等级 (1.47 mm) | HB |
| UL 94 |
极限氧指数 | 22 | % | ASTM D2863 |
| 注射 | 额定值 | 单位制 |
|
干燥温度 | 104 到 110 | °C | |
干燥时间 | 3.0 到 | hr | |
干燥时间，最大 | 8.0 | hr | |
建议的最大水分含量 | 0.020 | % | |
建议注入量 | 30 到 70 | % | |
螺筒后部温度 | 249 到 299 | °C | |
螺筒中部温度 | 260 到 304 | °C | |
螺筒前部温度 | 271 到 310 | °C | |
射嘴温度 | 282 到 310 | °C | |
加工（熔体）温度 | 282 到 310 | °C | |
模具温度 | 76.7 到 104 | °C | |
背压 | 0.345 到 0.689 | MPa | |
螺杆转速 | 20 到 100 | rpm |