LNP* Lubricomp* Compound KL004 | Americas: COMMERCIAL |
| Also known as: 404 |
| Product Reorder Name: KL004 |
| LNP Lubricomp* KL004 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. This grade was previously found under the LNP* Fulton* Tradename. |
| Property |
| TYPICAL PROPERTIES(1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yield | 51 | MPa | ASTM D 638 | |
| Tensile Stress, break | 50 | MPa | ASTM D 638 | |
| Tensile Strain, yield | 11 | % | ASTM D 638 | |
| Tensile Strain, break | 18 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 2130 | MPa | ASTM D 638 | |
| Flexural Stress | 75 | MPa | ASTM D 790 | |
| Flexural Modulus | 2060 | MPa | ASTM D 790 | |
| Tensile Stress, yield | 47 | MPa | ISO 527 | |
| Tensile Stress, break | 46 | MPa | ISO 527 | |
| Tensile Strain, yield | 10 | % | ISO 527 | |
| Tensile Strain, break | 23 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 | |
| Flexural Stress | 79 | MPa | ISO 178 | |
| Flexural Modulus | 2600 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 640 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D 256 | |
| Instrumented Impact Energy @ peak, 23°C | 6 | J | ASTM D 3763 | |
| Multiaxial Impact | 0 | J | ISO 6603 | |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 157 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 99 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 1.1E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.11E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 1.1E-04 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 1.11E-04 | 1/°C | ISO 11359-2 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Density | 1.5 | g/cm³ | ASTM D 792 | |
| Moisture Absorption, 50% RH, 24 hrs | 0.15 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 24 hrs | 1.97 - 2.5 | % | ASTM D 955 | |
| Mold Shrinkage, xflow, 24 hrs | 1.97 - 2.5 | % | ASTM D 955 | |
| Mold Shrinkage, flow, 24 hrs | 1.97 - 2.5 | % | ISO 294 | |
| Mold Shrinkage, xflow, 24 hrs | 1.97 - 2.5 | % | ISO 294 | |
| Wear Factor Washer | 15 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified | |
| Dynamic COF | 0.29 | - | ASTM D 3702 Modified | |
| Static COF | 0.15 | - | ASTM D 3702 Modified | |
| Density | 1.5 | g/cm³ | ISO 1183 | |
| Moisture Absorption (23°C / 50% RH) | 0.26 | % | ISO 62 | |
| Source GMD, last updated:10/04/2004 |