供应韩国三星HIPS vh-1800 tt 注塑级 vh-1800 tt
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 200℃/5.0kg | ASTM D-1238 | 10 | g/10min |
| 吸水率 | 24hr | ASTM D-570 | 0.070 | % |
| 物理性能 | 比重 | | ASTM D-792 | 1.16 | g/cm3 |
| 模具收缩率 | Flow | ASTM D-955 | 0.40-0.70 | % |
| 机械性能 | 洛氏硬度 | | ASTM D-785 | 90 | R-Scale |
| 拉伸断裂强度 | | ASTM D-638 | 24.5 | MPa |
| 拉伸断裂伸长率 | | ASTM D-638 | 35 | % |
| 弯曲模量 | | ASTM D-790 | 2160 | MPa |
| 弯曲强度 | | ASTM D-790 | 34.1 | MPa |
| IZOD缺口冲击强度 | 23℃，3.18mm | ASTM D-256 | 97.7 | J/m |
| IZOD缺口冲击强度 | 23℃，6.35mm | ASTM D-256 | 58.7 | J/m |
| 电气性能 | 表面电阻率 | | ASTM D-257 | 1.0E+14 | Ohms |
| 体积电阻率 | | ASTM D-257 | 1.0E+18 | Ohm.cm |
| 热性能 | 热变形温度 | 0.45MPa，未退火，6.35mm | ASTM D-648 | 81.1 | ℃ |
| 热变形温度 | 1.80MPa，未退火，6.35mm | ASTM D-648 | 72.8 | ℃ |
| 维卡软化温度 | | ASTM D-1525 | 86.1 | ℃ |
| 阻燃性 | 1.59mm | UL 94 | V-0 | |
| 阻燃性 | 2.54mm | UL 94 | V-0 | |
| 阻燃性 | 3.18mm | UL 94 | V-0 | |