销售供应聚甲醛 赛钢 耐磨损 抗静电POM FV-30
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | | ASTM D-1238 | 30 | g/10 min |
| 物理性能 | 吸收率 | 23°C,60%RH | ASTM D-570 | 0.22 | % |
| 比重 | | ASTM D-792 | 1.41 | |
| 成型收缩率 | t3mm,直径100mm | | 2.0 | % |
| 机械性能 | 拉伸强度 | 23℃ | ASTM D-638 | 610 | kgf/cm2 |
| IZOD冲击强度 | Notch t3.2mm | ASTM D-256 | 6.0 | kgf.cm/cm |
| 曲折弹性率 | 23℃ | ASTM D-790 | 2.65 | ×104kgf/cm2 |
| 弯曲强度 | 23℃ | ASTM D-790 | 900 | kgf/cm2 |
| 拉伸冲击强度 | t3.2mm S type | ASTM D-1822 | 110 | kgf.cm/cm2 |
| 洛氏硬度 | M scale | ASTM D-785 | M80 | |
| 伸缩率 | 23℃ | ASTM D-638 | 40 | % |
| 断裂强度 | t2mm | ASTM D-732 | 560 | kgf/cm2 |
| 电气性能 | 导电率 | 106Hz | ASTM D-150 | 3.7 | |
| 个质损耗系数 | 106Hz | ASTM D-150 | 0.007 | |
| 体积电阻率 | | ASTM D-257 | 1×1012 | Ω.cm |
| 耐电压 | | ASTM D-149 | 19 | KV/mm |
| 表面电阻率 | | ASTM D-257 | 1×1013 | Ω |
| 热性能 | 线膨胀系数 | 20C°-80C° | ASTM D-696 | 13 | ×10-5cm/cm/℃ |
| 热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 158 | ℃ |
| 热变形温度 | 18.6kgf/cm2 | ASTM D-648 | 110 | ℃ |
| 熔点 | 10C°/min | DSC Method | 165 | ℃ |
| 燃烧性 | t0.8mm | UL 94 | HB | |