PSU/德国巴斯夫/S2010G4/高刚性/量大从优货源稳定/印刷机料/塑料
'
Ultrason® S 2010 G4 聚砜 20% 玻璃纤维增强材料 |
Ultrason S 2010 G4 is a 20% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength.
Applications
Typical applications include circuit braker parts, lamp holders, heat shields, impellers, and printer cartridges. |
材料状态 | |
资料 1 | - Processing - Injection Molding Guide (English)
| - Technical Datasheet (English)
| |
|
UL 黄卡 2 | |
搜索 UL 黄卡 | |
供货地区 | |
填料/增强材料 | |
性能特点 | |
用途 | |
机构评级 | |
RoHS 合规性 | |
形式 | |
加工方法 | |
多点数据 | - Creep Modulus vs. Time (ISO 11403-1)
- Isochronous Stress vs. Strain (ISO 11403-1)
| - Isothermal Stress vs. Strain (ISO 11403-1)
- Secant Modulus vs. Strain (ISO 11403-1)
| - Viscosity vs. Shear Rate (ISO 11403-2)
|
|
密度 | 1.38 | g/cm³ | ISO 1183 |
溶化体积流率（MVR） (360°C/10.0 kg) | 40.0 | cm³/10min | ISO 1133 |
收缩率 | | | ISO 294-4 |
横向流量 | 0.52 | % | |
流量 | 0.31 | % | |
吸水率 | | | ISO 62 |
饱和, 23°C | 0.70 | % | |
平衡, 23°C, 50% RH | 0.20 | % | |
拉伸模量 (23°C) | 6800 | MPa | ISO 527-2 |
拉伸应力 (断裂, 23°C) | 110 | MPa | ISO 527-2 |
拉伸应变 (断裂, 23°C) | 2.2 | % | ISO 527-2 |
拉伸蠕变模量 (1000 hr) | 6000 | MPa | ISO 899-1 |
简支梁缺口冲击强度 | | | ISO 179 |
-30°C | 7.0 | kJ/m² | |
23°C | 7.0 | kJ/m² | |
简支梁缺口冲击强度 | | | ISO 179 |
-30°C | 45 | kJ/m² | |
23°C | 45 | kJ/m² | |
悬壁梁缺口冲击强度 (23°C) | 7.0 | kJ/m² | ISO 180 |
热变形温度 (1.8 MPa, 未退火) | 183 | °C | ISO 75-2/A |
线形膨胀系数 - 流动 | 0.000026 | cm/cm/°C | |
RTI Elec (1.50 mm) | 160 | °C | UL 746 |
RTI Imp (1.50 mm) | 140 | °C | UL 746 |
RTI Str (1.50 mm) | 160 | °C | UL 746 |
表面电阻率 | > 1.0E+14 | ohm | IEC 60093 |
体积电阻率 | > 1.0E+15 | ohm·cm | IEC 60093 |
耐电强度 | 46 | kV/mm | IEC 60243-1 |
介电常数 | | | IEC 60250 |
100 Hz | 3.50 | | |
1 MHz | 3.50 | | |
耗散因数 | | | IEC 60250 |
100 Hz | 0.0010 | | |
1 MHz | 0.0060 | | |
漏电起痕指数 | 125 | V | IEC 60112 |
UL 阻燃等级 (1.50 mm) | V-1 | | UL 94 |
'