RTP 3400 FC-110
Liquid Crystal Polymer (LCP)
Glass Fiber
UL94 V-0
|
PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS |
PERMANENCE | English | | SI Metric | | ASTM
TEST | | | | Specific Gravity | 1.68 | | 1.68 | | D 792 | | Molding Shrinkage | | | 1/8 in (3.2 mm) section | 0.0005 - 0.0020 in/in | | 0.05 - 0.20 % | | D 955 | | Water Absorption, 24 hrs @ 23°C | 0.100 % | | 0.100 % | | D 570 |
MECHANICAL | | | | Impact Strength, Izod | | | notched 1/8 in (3.2 mm) section | 1.2 ft-lbs/in | | 64 J/m | | D 256 | | unnotched 1/8 in (3.2 mm) section | 8.5 ft-lbs/in | | 454 J/m | | D 4812 | | Tensile Strength | 15000 psi | | 103 MPa | | D 638 | | Tensile Elongation | 1.0 - 2.0 % | | 1.0 - 2.0 % | | D 638 | | Tensile Modulus | 2.00 x 10^6 psi | | 13790 MPa | | D 638 | | Flexural Strength | 20000 psi | | 138 MPa | | D 790 | | Flexural Modulus | 1.85 x 10^6 psi | | 12756 MPa | | D 790 |
THERMAL | | | | Deflection Temperature | | | @ 264 psi (1820 kPa) | 600 °F | | 316 °C | | D 648 | | Ignition Resistance* | | | Flammability | V-0 @ 0.019 in | | V-0 @ 0.4 mm | | UL94 | | | | PROPERTY NOTES | | | Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties. | | * This rating is not intended to reflect hazards of this or any other material under actual fire conditions. |
GENERAL PROCESSING FOR INJECTION MOLDING | | | English | | SI Metric | | | | | | Injection Pressure | 10000 - 18000 psi | | 69 - 124 MPa | | | | Melt Temperature | 685 - 750 °F | | 363 - 399 °C | | | | Mold Temperature | 150 - 200 °F | | 66 - 93 °C | | | | Drying | 8 hrs @ 300 °F | | 8 hrs @ 149 °C | | | | Dew Point | -20 °F | | -29 °C |
|
|
|
美国RTP Compounds LCP 3400-G-640：LCP日本杜邦原料物性描述 液晶聚合树脂不仅能够承受高温… 而且具有卓越的全面性能，可提高模塑生产率。 用其取代陶瓷、热固性塑料、PPS 塑料或其他种类的 LCP 塑料，则可缩小零件尺寸， 改进性能，加快生产速度、降低系统成本，有助于开发新的市场。这种塑料具有下列特 
美国RTP Compounds LCP 3400-G-640：ProductDescription
|
| RTP 3401-1 | Glass Fiber 10% |
| RTP 3403-1 | Glass Fiber 20% |
| RTP 3405-1 | Glass Fiber 30% |
| RTP 3407-1 | Glass Fiber 40% |
| RTP 3400-3 | Unreinforced Base Resin (Precolor Only) |
| RTP 3401-3 | Glass Fiber 10% |
| RTP 3402-3 | Glass Fiber 15% |
美国RTP Compounds LCP 3400-G-640：特点和性能： 高温电气/电子装配：能承受 SMT 装配工序操作，包括无铅回流焊接。卓越的热老化性 能，在高温下保持固有特性。 设计灵活性：卓越的流动性 - 长路径，薄壁，复杂的形状，优异的耐化学腐蚀性。 精确度：尺寸稳定性极佳，模塑收缩率低，热膨胀率低。 模塑速度：周期循环极快，劲度、强度和韧度的完美平衡。 卓越的抗蠕变性，在宽广的温度范围内具有卓越的介电性能。