薄膜 高刚性 高强度 HDPE/大韩油化/F600 hdpe薄膜
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 吸水率 | | ASTM D-570 | >0.01 | % |
| 熔体流动速率 | | ASTM D-1238 | 0.035 | g/10min |
| 密度 | | ASTM D-792 | 0.957 | g/cm3 |
| 断裂伸张率 | | ASTM D-638 | | % |
| 洛氏硬度 | | ASTM D-785 | 47 | scRale |
| 抗动变应力 | | ASTM D-1693 | | hr.cond.B100% |
| 冲击强度 | 带缺口 | ASTM D-256 | | kgf.cm/cm |
| 成型收缩率 | 线型 | KPIC Method | 1.5-2.5 | % |
| 拉伸强度 | | ASTM D-638 | 400 | kgf/cm2 |
| 挠曲模量 | | ASTM D-790 | 10,000 | kgf/cm2 |
| 损耗因素 | | ASTM D-150 | 2 | 10-4 |
| 体积电阻率 | | ASTM D-1525 | 123 | ℃ |
| 绝缘强度 | | ASTM D-149 | 48 | KV/mm |
| 体积电阻率 | | ASTM D-257 | 1 | 1017ohm.cm |
| 介电常数 | | ASTM D-150 | 2.3 |
| 易变温度 | | ASTM D-746 | >-70 | ℃ |
| 熔点 | | ASTM D-3418 | 134 | ℃ |
| 热变形温度 | | ASTM D-648 | 62 | ℃ |
| 比热容 | | KPIC Method | 0.45 | cal/g℃ |
| 线性膨胀系数 | | ASTM D-696 | 1.5 | 10-5cm/cm°C |