性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
吸水率 | 24hr | ASTM D-570 | DAM|50%RH,0.5|- | % |
比重 | ASTM D-792DAM|50%RH,1.56|- |
模具收缩率 | 3.2mm flow | ASTM D-792 | DAM|50%RH,0.4|- | % |
弯曲强度 | ASTM D-790DAM|50%RH,240|-MPa |
断裂伸长率 | ASTM D-638DAM|50%RH,2.5|4% |
IZOD缺口冲击强度 | ASTM D-256DAM|50%RH,100|105J/m |
弯曲模量 | ASTM D-790DAM|50%RH,8960|6900MPa |
拉伸强度 | ASTM D-638DAM|50%RH,169|134MPa |
体积电阻率 | ASTM D-257DAM|50%RH,10,14,|10,11Ω.cm |
损耗因数 | 103Hz | ASTM D-150 | DAM|50%RH,DAM|50%RH,0.|541,0.009|0.113 |
介电常数 | 103Hz | ASTM D-150 | DAM|50%RH,3.6|5.1 |
表面电阻率 | ASTM D-257DAM|50%RH,10,14,|10,11Ω |
介电强度 | 3.2mm | ASTM D-149 | DAM|50%RH,17.2|15.6 | kv/mm |
损耗因数 | 106Hz | ASTM D-150 | DAM|50%RH,0.014|0.041 |
介电常数 | 106Hz | ASTM D-150 | DAM|50%RH,3.5|3.8 |
热变形温度 | 0.45MPa | ASMT D-648 | DAM|50%RH,257|- | ℃ |
热变形温度 | 1.80MPa | ASTM D-648 | DAM|50%RH,235|- | MPa |
熔点 | ASTM D-3418DAM|50%RH,262|-℃ |