目数 丝径 | 目数 | 编织结构 | 开孔大小 | 丝径 | 开孔率 | 丝网厚度 | 允许误差 | 过墨量 | 重量 |
Mesh Count and Diameter (Mesh/cm μm) | Mesh Count (Mesh/inch) | Weave | Aperture (μm) | Thread Diameter (μm) | Opening (%) | Thickness (μm) | Thickness Tolerance (μm) | Theoretical Ink deposit (cm3/m2) | Weight (g/m2) |
13-150PW(SL) | 33 | 1:1 | 619 | 150 | 64 | 300 | 14 | 128 | 60 |
21-80PW (S) | 55 | 1:1 | 296 | 80 | 69 | 120 | 9 | 79 | 35 |
21-150PW(SL) | 55 | 1:1 | 326 | 150 | 46 | 260 | 14 | 118 | 121 |
24-100PW(T) | 60 | 1:1 | 316 | 100 | 57 | 136 | 11 | 65 | 81 |
28-140PW(SL) | 70 | 1:1 | 217 | 140 | 40 | 195 | 13 | 76 | 125 |
32-55PW(S) | 81 | 1:1 | 257 | 55 | 67 | 103 | 6 | 67 | 28 |
32-64PW(S) | 81 | 1:1 | 248 | 64 | 63 | 95 | 6 | 56 | 32 |
32-100PW(T) | 81 | 1:1 | 212 | 100 | 45 | 165 | 8 | 73 | 75 |
36-90PW(T) | 92 | 1:1 | 183 | 90 | 44 | 150 | 8 | 65 | 68 |
39-55PW(S) | 100 | 1:1 | 177 | 55 | 56 | 88 | 6 | 55 | 30 |
43-80PW(T) | 110 | 1:1 | 149 | 80 | 41 | 130 | 7 | 53 | 64 |
47-45PW(S) | 120 | 2:2 | 166 | 45*2 | 61 | 80 | 6 | 42 | 40 |
47-55PW(S) | 120 | 1:1 | 152 | 55 | 51 | 88 | 6 | 48 | 34 |
48-70PW(T) | 122 | 1:1 | 133 | 70 | 41 | 115 | 6 | 47 | 55 |
53-45PW(S) | 135 | 2:2 | 143 | 45*2 | 57 | 79 | 7 | 41 | 46 |
53-55PW(S) | 135 | 1:1 | 133 | 55 | 50 | 86 | 6 | 42 | 40 |
54-64PW(T) | 137 | 1:1 | 115 | 64 | 39 | 100 | 5 | 39 | 51 |
涤纶是合成纤维中的一个重要品种,是我国聚酯纤维的商品名称。它是以精对苯二甲酸(PTA)或对苯二甲酸二甲酯(DMT)和乙二醇(EG)为原料经酯化或酯交换和缩聚反应而制得的成纤高聚物——聚对苯二甲酸乙二醇酯(PET),经纺丝和后处理制成的纤维。
1.强度高。涤纶短纤维强度为2.6~5.7cN/dtex,高强力纤维为5.6
涤纶
~
8.0cN/dtex。涤纶由于吸湿性较低,它的湿态强度与干态强度基本相同。耐冲击强度比锦纶高4倍,比粘胶纤维高20倍。
2.弹性好。涤纶弹性接近羊毛,当伸长5%~6%时,几乎可以完全恢复。耐皱性超过其他纤维,即织物不折皱,尺寸稳定性好。弹性模数为22~141cN/dtex,比锦纶高2~3倍。
3.涤纶耐热性和热稳定性在合成纤维织物中是最好的。
4.涤纶表面光滑,内部分子排列紧密。
5.涤纶耐磨性好。耐磨性仅次于耐磨性最好的锦纶,比其他天然纤维和合成纤维都好。
6.涤纶耐光性好。耐光性仅次于腈纶。
7.涤纶耐腐蚀。可耐漂白剂、氧化剂、烃类、酮类、石油产品及无机酸。耐稀碱,不怕霉,但热碱可使其分解。