| 产品说明 | |
PPE+PS blend. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant (restrictions apply). Combines good hydrolytic stability and dimensional stability. |
性能特点 |
| |||
用途 |
| |||
机构评级 |
| |||
加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
比重 | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
熔流率 (280°C/5.0 kg) | 9.2 | g/10 min | ASTM D1238 |
溶化体积流率（MVR） (280°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
收缩率 | Internal Method | ||
流动 : | 0.50 到 0.70 | % | |
横向流动 : | 0.50 到 0.70 | % | |
吸水率 | |||
24 hr | 0.060 | % | ASTM D570 |
饱和, 23°C | 0.23 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.060 | % | ISO 62 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
洛氏硬度 (R 计秤) | 119 |
| ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | |||
-- 2 | 2860 | MPa | ASTM D638 |
-- | 2300 | MPa | ISO 527-2/1 |
抗张强度 | |||
屈服 3 | 58.6 | MPa | ASTM D638 |
屈服 | 55.0 | MPa | ISO 527-2/50 |
断裂 3 | 49.6 | MPa | ASTM D638 |
断裂 | 50.0 | MPa | ISO 527-2/50 |
伸长率 | |||
屈服 3 | 7.2 | % | ASTM D638 |
屈服 | 5.0 | % | ISO 527-2/50 |
断裂 3 | 28 | % | ASTM D638 |
断裂 | 30 | % | ISO 527-2/50 |
弯曲模量 | |||
50.0 mm 跨距 4 | 2650 | MPa | ASTM D790 |
100 mm 跨距 5 | 2420 | MPa | ASTM D790 |
-- 6 | 2200 | MPa | ISO 178 |
弯曲强度 | |||
-- 6, 7 | 75.0 | MPa | ISO 178 |
屈服, 50.0 mm 跨距 4 | 90.3 | MPa | ASTM D790 |
屈服, 100 mm 跨距 5 | 89.6 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度 8 (23°C) | 15 | kJ/m² | ISO 179/1eA |
悬壁梁缺口冲击强度 | |||
-40°C | 130 | J/m | ASTM D256 |
23°C | 210 | J/m | ASTM D256 |
-30°C 9 | 5.0 | kJ/m² | ISO 180/1A |
23°C 9 | 15 | kJ/m² | ISO 180/1A |
装有测量仪表的落镖冲击 (23°C, Total Energy) | 48.8 | J | ASTM D3763 |
落锤冲击 | ASTM D3029 | ||
-40°C | 5.42 | J | |
-30°C | 25.8 | J |
| 热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 | |||
0.45 MPa, 未退火, | 132 | °C | ASTM D648 |
0.45 MPa, 未退火, | 137 | °C | ASTM D648 |
1.8 MPa, 未退火, | 118 | °C | ASTM D648 |
1.8 MPa, 未退火, | 127 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 10 | 115 | °C | ISO 75-2/Af |
维卡软化温度 | |||
-- | 149 | °C | ASTM D1525 11 |
-- | 135 | °C | ISO 306/B50 |
-- | 140 | °C | ISO 306/B120 |
线形膨胀系数 | |||
流动 : -40 到 40°C | 0.000092 | cm/cm/°C | ASTM E831 |
流动 : -40 到 40°C | 0.000070 | cm/cm/°C | ISO 11359-2 |
横向 : -40 到 40°C | 0.000095 | cm/cm/°C | ASTM E831 |
横向 : -40 到 40°C | 0.000070 | cm/cm/°C | ISO 11359-2 |
RTI Elec | 105 | °C | UL 746 |
RTI Imp | 90.0 | °C | UL 746 |
RTI Str | 105 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
介电强度 (3.20 mm, in Oil) | 22 | kV/mm | ASTM D149 |
介电常数 | ASTM D150 | ||
50 Hz | 2.65 |
| |
60 Hz | 2.65 |
| |
耗散因数 | ASTM D150 | ||
50 Hz | 0.00040 |
| |
60 Hz | 0.00040 |
| |
耐电弧性 12 | PLC 7 |
| ASTM D495 |
相比耐漏电起痕指数(CTI) | PLC 3 |
| UL 746 |
高电弧燃烧指数(HAI) | PLC 0 |
| UL 746 |
高电压电弧起痕速率 (HVTR) | PLC 4 |
| UL 746 |
热丝引燃 (HWI) | PLC 2 |
| UL 746 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
UL 阻燃等级 (1.47 mm) | HB |
| UL 94 |
极限氧指数 | 22 | % | ASTM D2863 |
| 注射 | 额定值 | 单位制 |
|
干燥温度 | 104 到 110 | °C | |
干燥时间 | 3.0 到 | hr | |
干燥时间，最大 | 8.0 | hr | |
建议的最大水分含量 | 0.020 | % | |
建议注入量 | 30 到 70 | % | |
螺筒后部温度 | 249 到 299 | °C | |
螺筒中部温度 | 260 到 304 | °C | |
螺筒前部温度 | 271 到 310 | °C | |
射嘴温度 | 282 到 310 | °C | |
加工（熔体）温度 | 282 到 310 | °C | |
模具温度 | 76.7 到 104 | °C | |
背压 | 0.345 到 0.689 | MPa | |
螺杆转速 | 20 到 100 | rpm |