②原料技术数据
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
--- |
ASTM D-1238 |
12 |
g/10min |
| 比重 |
--- |
ASTM D-792 |
1.05 |
g/cm3 |
| 物理性能 |
收缩率 |
--- |
ASTM D-955 |
0.4-0.7 |
% |
| 机械性能 |
洛氏硬度 |
--- |
ASTM D-785 |
L-70 |
--- |
| IZOD缺口冲击强度 |
--- |
ASTM D-256 |
2.2 |
Kg-cm/cm |
| 拉伸屈服强度 |
--- |
ASTM D-638 |
420 |
kg/cm2 |
| 断裂伸长率 |
--- |
ASTM D-638 |
2 |
% |
| 挠曲强度 |
--- |
ASTM D-790 |
75 |
kg/cm2 |
| 加工性能 |
揉曲模量 |
--- |
ASTM D-790 |
29000 |
kg/cm2 |
| 加工溶融温度 |
--- |
--- |
200-240 |
℃ |
| 热 性 能 |
干燥温度 |
--- |
--- |
70 |
DEG |
| 可燃性 |
--- |
UL-94 |
HB |
--- |
| 热变形温度 |
--- |
ASTM D-648 |
71 |
℃ |
| 维卡软化点 |
--- |
ASTM D-1525 |
91 |
℃ |
| 维卡软化点 |
5kg |
ASTM D-1525 |
86 |
℃ | | |