HDPE/美国陶氏/DMDA-8007 高刚性,高光泽
'
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 流动率 | 190℃/21.6kg | ASTM D-1238 | 180 | g/10min |
| 密度 | | ASTM D-792 | 0.965 | g/cm3 |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 8.25 | g/10min |
| 机械性能 | 屈服拉伸强度 | | ASTM D-638 | 4500(31) | psi(MPa) |
| 耐环境应力开裂性 | 122?H(50℃),F50,100%lgepal | ASTM D-1693 | 2 | hrs |
| 拉伸冲击强度 | | ASTM D-1822,Type S | 80(168) | ft?lb/in2(kJ/m2) |
| 2%割线弯曲模量 | | ASTM D-790 B | 205,000(1413) | psi(MPa) |
| 肖氏硬度 | | ASTM D-2240 | 61 | Shore D |
| 断裂拉伸强度 | | ASTM D-638 | 2600(18) | psi(MPa) |
| 屈服伸长率 | | ASTM D-638 | 6 | % |
| 断裂伸长率 | | ASTM D-638 | 354 | % |
| 热性能 | 脆化温度 | | ASTM D-746 | <-105(<-76) | ℉(℃) |
| 维卡软化点 | | ASTM D-1525 | 268(131) | ℉(℃) |
| DSC结晶点 | | Dow Method | 248(120) | ℉(℃) |
| 热变形温度 | 66psi(0.45MPa) | ASTM D-648 | 183(84) | ℉(℃) |
| DSC熔点 | | Dow Method | 271(133) | ℉(℃) |
'