ABS/DG-417/天津大沽
| | 原料技术数据 | | | | | | | 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | | 机械性能 | 拉伸强度 | 1/8",50mm/min | ASTM
D-638 | 510 | kg/cm2 | | 拉伸率 | 1/8",50mm/min | ASTM
D-638 | 40 | % | | 弯曲强度 | 1/8",1.3mm/min | ASTM
D-790 | 770 | kg/cm2 | | 弯曲模量 | 1/8",1.3mm/min | ASTM
D-790 | 25180 | kg/cm2 | | IZOD冲击强度 | 1/8",23℃ | ASTM
D-256 | 25 | kg.cm/cm | | 洛氏硬度 | | ASTM
D-785 | 112 | R
Scale | | 热性能 | 热变形温度 | 1/8",1.8MPa | ASTM
D-648 | 80 | ℃ | | 维卡软化点 | 1kg | ASTM
D-1525 | 99 | ℃ | | 燃烧热 | 1/8" | UL
94 | HB | | | 物理性能 | 流动系数 | 220℃/10kg | ASTM
D-1238 | 15.5 | g/10min | | 比重 | 23℃ | ASTM
D-792 | 1.045 | | | 成型收缩率 | | ASTM
D-955 | 0.5-0.8 | % |
|
|
|