代理奇美abs pa-777e ABS树脂 原料价格 高耐热/发热家电外壳
|
|
|
|
|
| 产品参数 | 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | | 物理性能 | 比重 | | ASTM D-792 | 1.07 | 23/23℃ | | 熔体流动速率 | 220℃×10kg | ISO-1133 | 5.0 | g/10min | | 机械性能 | 洛氏硬度 | | ASTM D-785 | 115 | R | | IZOD冲击强度 | 1/8" | ASTM D-256 | 12 | kg.cm/cm | | 弯曲强度 | | ASTM D-790 | 10630 | lb/in2 | | IZOD冲击强度 | 1/4〃 | ASTM D-256 | 11 | kg.cm/cm | | 弯曲强度 | | ASTM D-790 | 750 | kg/cm2 | | 引张强度 | | ASTM D-638 | 6240 | lb/in2 | | 引张强度 | | ASTM D-638 | 440 | kg/cm2 | | 弯曲弹性率 | | ASTM D-790 | 2.5×104 | kg/cm2 | | IZOD冲击强度 | 1/8" | ASTM D-256 | 2.2 | ft.lb/in | | 弯曲弹性率 | | ASTM D-790 | 3.5×105 | lb/in2 | | IZOD冲击强度 | 1/4〃 | ASTM D-256 | 2.0 | ft.lb/in | | 热性能 | 维卡软化点 | | ASTM D-1525 | 264 | ℉ | | 热变形温度 | | ASTM D-648 | 109(228) | ℉ | | 热变形温度 | | ASTM D-648 | 120(248) | ℃ | | 燃烧性 | File No. E56070 UL&C-UL | | 1/16"HB | | | 维卡软化点 | | ASTM D-1525 | 129 | ℃ |
| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | - | % | | 热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 107(225) | ℃（℉） | | 未退火 | ASTM D648/ISO 75 | 97(207) | ℃（℉） | | 维卡软化点 | | ASTM D1525/ISO R306 | 115(239) | ℃（℉） | | 熔点 | | - | - | ℃（℉） | | 燃烧性（率） | | UL94 | 1.6mmHB | | | 线性膨胀系数 | | ASTM D696/ISO 11359 | - | mm/mm.℃ | | 加工条件 | 干燥条件 | | | 90~95°C下烘料约3小时 | | | 加工温度 | 射嘴 | | 220~250°C | ℃ | | 料筒前段 | | 230~250 °C | ℃ | | 料筒中段 | | 230~250 ° | ℃ | | 料筒后段 | | 220~240 ° | ℃ | | 熔体温度 | | | - | ℃ | | 模具温度 | | | 30~70°C | ℃ | | 压力 | 注塑压力 | | 50~70kg/cm² | Mpa | | 保压压力 | | 40~60kg/cm² | Mpa | | 背压 | | 5~15kg/cm² | Mpa | | 螺杆转速 | | | - | rpm | | 其他 | 备注 | 在射出周期中勿将热融胶长期停留在加热管中 | | 颜色 | - | | 特性 | 耐热性、高冲击强度 | | 用途 | 发热家电外壳 / 乾发吹风筒 / 熨斗外壳 / 暖风机 / 汽车零配件如仪表板 / 水箱护罩等 |
自定义内容 |
| 1/8〃 50℃/hr | ASTM D-1525 | 104 | ℃ |