Description
THYOSIL E1610 is an acrylic emulsion specially designed for manufacturing gloss to matt interior parquet lacquers. It supplies high traffic resistance, excellent hardness, high gloss and durability.
是一款水性丙烯酸乳液聚合物，为高光泽和哑光室内地板漆所设计 ，它支持耐高流量性，优异的硬度，高光泽和耐久性。
Characteristics特点
· The crosslinking technology offers improved resistance properties versus conventional polymers.
· 优异的自交联技术 提供来了高硬度，高光，耐候性能。
· The low solvent requirement to formulate offers improved performance.
· 低溶剂配方提供了优异的性能，外观，以及各种耐性。
· Once dried the excellent dry film clarity provided by THYOSIL E1610 enhances the beauty of the wood.
· 一旦干燥优异的干膜的清晰度提高了木材的美丽外观。
Advantages 优势
ü Very good wet and dry film appearance. 非常好的干湿膜外观
ü Excellent block resistance. 优异的防结皮性和持久性
ü Good sandability.良好的打磨性
ü No wood discoloration.没有木材变色
ü Very good resistance to household chemicals..好的耐各种家用化学品腐蚀性能
ü Compatible with PU resins. 与PU树脂兼容
Typical properties典型值
These properties are typical, do not constitute specifications
Appearance外观 | Milky white liquid 乳白色液体 |
Solids % 固含量 | 45 |
pH | 8.0 |
Viscosity a 25ºC (cP)粘度 | 500 |
MFFT (ºC) 成膜温度 | 30 |
GLOSS PARQUET LACQUER 光泽实木复合地板漆 -THYOSIL E1610- | |
Raw material 原料 | (%) |
THYOSIL E1610 | 76,00 |
THYON PW7聚乙烯蜡乳液 | 0.50 |
BYK-346 (1) 润湿剂 | 0.05 |
NX / 795 (2) 新戊二醇单异丁酸酯 （凝聚剂） | 1.60 |
Water 水 | 15.90 |
Butyl Glycol丁基乙二醇 | 4.40 |
THYON T25 DPM 流平润湿剂 | 0.05 |
BYK-024 (1) 消泡剂 | 0.80 |
BYK-028 (1) 消泡剂 | 0.30 |
Tafigel Pur 80 (3) 聚氨酯增稠剂 | 0.40 |
Total | 100,00 |
Typical properties:典型值
Test | Result |
Solid Content 固含量 | 35% |
Viscosity Ford Cup N°4 at25°C | 粘度20 sec秒 |
pH | 8.6 |
Gloss (Glossmeter 60º)光度 | 75 |
Adhesion (ASTM D3359)附着力 | Pass |
Hardness (ASTM D3363)硬度 | 3 H |
SATIN PARQUET LACQUER 缎面（哑光）实木复合地板 -THYOSIL E1610- | |
Raw material 原料 | (%) |
THYOSIL E1610 | 74,00 |
NX / 795 (1) 新戊二醇单异丁酸酯 | 凝聚剂3.00 |
Water 水 | 11.53 |
Butyl Glycol 丁基乙二醇 | 6.10 |
THYON T25 DPM 流平润湿剂 | 0.47 |
BYK-024 (2) 消泡剂 | 0.99 |
BYK-346 (2) 润湿剂 | 0.13 |
Syloid 244 (3) 胶态二氧化硅哑光粉 | 0.97 |
Kanowax 951210 D (4) | 0.81 |
THYON PW7 聚乙烯蜡分散液 | 1.00 |
Tafigel Pur 80 (5) 聚氨酯增稠剂 | 0.20 |
BYK-028 (2) 消泡剂 | 0.80 |
Total | 100,00 |
Typical properties典型值
Test | Result |
Solid Content 固含量 | 35% |
Viscosity Ford Cup N°4 at25°C | 粘度20 sec秒 |
pH | 8.6 |
Gloss (Glossmeter 60º)亮度 | 25 |
Adhesion (ASTM D3359)附着力 | Pass |
Hardness (ASTM D3363)硬度 | 2 H |
Starting formulations using THYOSIL E1610 and PU resin
GLOSS PARQUET LACQUER 光泽实木复合地板漆
-THYOSIL E1610 + PU resin（聚氨酯）- | |
Raw material | (%) |
THYOSIL E1610 | 64,00 |
NX / 795 (1) 新戊二醇单异丁酸酯（凝聚剂） | 1.60 |
Water 水 | 15.85 |
Butyl Glycol 丁基乙二醇 | 4.40 |
THYON T25 DPM 流平润湿剂 | 0.05 |
BYK-024 (2) 消泡剂 | 0.80 |
BYK-346 (2) 润湿剂 | 0.10 |
BYK-028 (2) 消泡剂 | 0.30 |
THYON PW7 聚乙烯蜡分散液 | 0.50 |
Bahydrol uh 2593/1 (3) 水性聚氨酯 | 12.00 |
Tafigel Pur 80 (4) 聚氨酯增稠剂 | 0.40 |
Total | 100,00 |
Typical properties: 典型值
Test 测试 | Result结果 |
Solid Content 固含量 | 35% |
Viscosity Ford Cup N°4 at25°C | 粘度20 sec秒 |
pH | 8.6 |
Gloss (Glossmeter 60º)亮度 | 75 |
Adhesion (ASTM D3359)附着力 | Pass |
Hardness (ASTM D3363) 硬度 | 2 H |
SATIN PARQUET LACQUER 缎面（哑光）实木复合地板 -THYOSIL E1610 + PU resin-（聚氨酯） | |
Raw material | (%) |
THYOSIL E1610 | 62,00 |
NX / 795 (1) 新戊二醇单异丁酸酯 | 凝聚剂3.00 |
Water 水 | 11.42 |
Butyl Glycol 丁基乙二醇 | 6.10 |
THYON T25 DPM 流平润湿剂 | 0.47 |
BYK-024 (2)消泡剂 | 1.10 |
BYK-346 (2) 润湿剂 | 0.13 |
Syloid 244 (3) 胶态二氧化硅哑光粉 | 0.97 |
Kanowax 951210 D (4) | 0.81 |
THYON PW7 聚乙烯蜡分散液 | 1.00 |
Bahydrol uh 2593/1 (5) 水性聚氨酯 | 12.00 |
Tafigel Pur 80 (6) 聚氨酯增稠剂 | 0.20 |
Total | 100,00 |
Typical properties 典型值
Test | Result |
Solid Content 固含量 | 35% |
Viscosity Ford Cup N°4 at25°C | 粘度20 sec秒 |
pH | 8.6 |
Gloss (Glossmeter 60º) 亮度 | 25 |
Adhesion (ASTM D3359)附着力 | Pass |
Hardness (ASTM D3363)硬度 | 2 H |
Chemical resistance 耐化学腐蚀性
The table below shows the resistance properties of THYOSIL E1610 exposed to various household products. Rating 0 to 5, 5 is best. 下表展示了E1610对各种家用化学品耐性，0到5级别中5是最好的
Testing procedure:测试步骤
Three
coats of the tested lacquers were brush applied over the wood. 在木上涂3次
After
one week drying at room temperature the household products were applied for one
hour on the lacquers surface.
室温下干放一周后，在涂层表面涂上家用化学品一个小时后测试。
PRODUCT | ACRYLIC LACQUER 丙烯酸漆 THYOSIL E1610 | ACRYLIC / PU LACQUER 丙烯酸漆+PU THYOSIL E1610 + PU |
Commercial oil 食用油 | 5 | 4 |
Detergent (1% )洗涤剂 | 5 | 4 |
Alcohol (1/1 water)酒精 | 3 | 2 |
Bleach (5%) 漂白剂 | 4 | 3 |
Coffee咖啡 | 5 | 4 |
Coke 可可 | 5 | 4 |
Vinegar 醋 | 3 | 2 |
Milk 奶 | 4 | 3 |
Butyl Glycol 丁基乙二醇 | 2 | 1 |
Acetone丙酮 | 0 | 0 |
Red wine 红酒 | 4 | 3 |
Yerba 马黛茶 | 5 | 4 |
Water 水 | 5 | 4 |
Abrasion resistance according to ASTM D4060耐磨损测试 参照 ASTM D4060标准
The following graph shows the weight loss of a THYOSIL E1610 based formulations and water based and solvent based commercial products after 500 and 1000 abrasion cycles. 下表展示了磨损500次和1000次的重量损失 Testing procedure:测试步骤
|
竖轴为减少的毫克数，横轴为不同原料做的面漆： E1610 ，E1610+PU配的漆，丙烯酸聚氨酯共聚物，水性聚氨酯。 蓝色为500圈，橙色为1000圈。
Safe handling Information
Before using this product, read carefully the Material Safety Data Sheet (MSDS).
Important: Avoid freezing. 注意防冻储存
Note: The statements above are based on the current state of knowledge. They are intended to describe the product in relation to necessary safety precautions, and should not be used as a warranty of any specific property. Revision: September 2013.