ABS/台湾奇美/PA-777B
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM D-792 | 1.03 | 23/23℃ |
| 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 6.7 | g/10min |
| 机械性能 | 引张强度 | | ASTM D-638 | 430 | kg/cm2 |
| 伸长率 | | ASTM D-638 | 15 | % |
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 3.7 | ft.lb/in |
| 弯曲强度 | | ASTM D-790 | 9920 | lb/in2 |
| 弯曲强度 | | ASTM D-790 | 700 | kg/cm2 |
| 弯曲弹性率 | | ASTM D-790 | 2.4×104 | kg/cm2 |
| 引张强度 | | ASTM D-638 | 6100 | lb/in2 |
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 20 | kg.cm/cm |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 4.3 | ft.lb/in |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 23 | kg.cm/cm |
| 弯曲弹性率 | | ASTM D-790 | 3.4×105 | lb/in2 |
| 洛氏硬度 | | ASTM D-785 | 112 | R |
| 热性能 | 维卡软化点 | | ASTM D-1525 | 239 | ℉ |
| 维卡软化点 | | ASTM D-1525 | 115 | ℃ |
| 热变形温度 | | ASTM D-648 | 97(206) | ℉ |
| 热变形温度 | | ASTM D-648 | 107(225) | ℃ |
| 燃烧性 | File No. E56070 UL&C-UL | | 1/16"HB | |