Nominal Value

Unit

Test Method

Density

1.20

g/cm³

Apparent Density 3

0.66

g/cm³

Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)

20

g/10 min

Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)

19.0

cm³/10min

Molding Shrinkage

Across Flow

0.50 to 0.70

%

Flow

0.50 to 0.70

%

Across Flow : 2.00 mm 4

0.70

%

Flow : 2.00 mm 4

0.65

%

Water Absorption

Saturation, 23°C

0.30

%

Equilibrium, 23°C, 50% RH

0.12

%

Nominal Value

Unit

Test Method

Ball Indentation Hardness

115

MPa

Nominal Value

Unit

Test Method

Tensile Modulus (23°C)

2400

MPa

Tensile Stress

Yield, 23°C

65.0

MPa

Break, 23°C

65.0

MPa

Tensile Strain

Yield, 23°C

6.0

%

Break, 23°C

130

%

Nominal Tensile Strain at Break (23°C)

> 50

%

Tensile Creep Modulus

1 hr

2200

MPa

1000 hr

1900

MPa

Flexural Modulus 5 (23°C)

2350

MPa

Flexural Stress 5

3.5% Strain, 23°C

73.0

MPa

23°C

97.0

MPa

Flexural Strain at Flexural Strength 6 (23°C)

7.1

%

Nominal Value

Unit

Test Method

Water Vapor Transmission Rate (23°C, 85% RH, 100 µm)

15

g/m²/24 hr

Oxygen Permeability

23°C, 25.4 µm

3200

cm³/m²/bar/24 hr

23°C, 100.0 µm

700

cm³/m²/bar/24 hr

Carbon Dioxide Permeability

23°C, 25.4 µm

18900

cm³/m²/bar/24 hr

23°C, 100.0 µm

4000

cm³/m²/bar/24 hr

Nitrogen Permeability

23°C, 25.4 µm

630

cm³/m²/bar/24 hr

23°C, 100.0 µm

130

cm³/m²/bar/24 hr

Nominal Value

Unit

Test Method

Charpy Notched Impact Strength 7

-30°C, Complete Break

14

kJ/m²

23°C, Partial Break

65

kJ/m²

Charpy Unnotched Impact Strength

-60°C

No Break

-30°C

No Break

23°C

No Break

Notched Izod Impact Strength 8

-30°C, Complete Break

12

kJ/m²

23°C, Partial Break

75

kJ/m²

Multi-Axial Instrumented Impact Energy

-30°C

65.0

J

23°C

55.0

J

Multi-Axial Instrumented Impact Peak Force

-30°C

6000

N

23°C

5100

N

Nominal Value

Unit

Test Method

Heat Deflection Temperature

0.45 MPa, Unannealed

137

°C

1.8 MPa, Unannealed

124

°C

Glass Transition Temperature 9

144

°C

Vicat Softening Temperature

--

145

°C

--

146

°C

Ball Pressure Test (136°C)

Pass

CLTE

Flow : 23 to 55°C

6.5E-5

cm/cm/°C

Transverse : 23 to 55°C

6.5E-5

cm/cm/°C

Thermal Conductivity 10 (23°C)

0.20

W/m/K

RTI Elec (1.50 mm)

125

°C

RTI Imp (1.50 mm)

115

°C

RTI Str (1.50 mm)

125

°C

Nominal Value

Unit

Test Method

Surface Resistivity

1.0E+16

ohm

Volume Resistivity (23°C)

1.0E+16

ohm·cm

Electric Strength (23°C, 1.00 mm)

34

kV/mm

Relative Permittivity

23°C, 100 Hz

3.10

23°C, 1 MHz

3.00

Dissipation Factor

23°C, 100 Hz

5.0E-4

23°C, 1 MHz

9.0E-3

Comparative Tracking Index

Solution A

250

V

Solution B

125

V

Nominal Value

Unit

Test Method

Flame Rating

2.70 mm

HB

0.360 mm

V-2

0.750 mm

V-2

Glow Wire Flammability Index

0.750 mm

850

°C

1.50 mm

875

°C

3.00 mm

930

°C

Glow Wire Ignition Temperature

0.750 mm

875

°C

1.00 mm

875

°C

1.50 mm

875

°C

3.00 mm

875

°C

Oxygen Index 11

27

%

Application of Flame from Small Burner 12 (2.00 mm)

K1, F1

Burning Rate 13 (< 1.00 mm)

Passed

Flash Ignition Temperature

480

°C

Needle Flame Test

Method F : 1.50 mm

1.0

min

Method F : 2.00 mm

2.0

min

Method F : 3.00 mm

2.0

min

Method K : 1.50 mm

0.1

min

Method K : 2.00 mm

0.1

min

Method K : 3.00 mm

0.2

min

Self Ignition Temperature

550

°C

Nominal Value

Unit

Test Method

Refractive Index 14

1.585

Transmittance

1000 µm

89.0

%

2000 µm

89.0

%

3000 µm

88.0

%

4000 µm

87.0

%

Haze (3000 µm)

< 0.80

%

Nominal Value

Test Method

Electrolytical Corrosion

A1

ISO Shortname

PC,MR,(,,)-18-9

Nominal Value

Unit

Processing (Melt) Temp

280 to 320

°C