供应挤出吹塑级PC 韩国LG 1261-03 水桶料
比重 | 1.20 | g/cm³ | ASTM D792 |
熔流率（熔体流动速率） (300°C/1.2 kg) | 2.5 | g/10 min | ASTM D1238 |
收缩率 -
流动
| 0.50 到 0.70 | % | ASTM D955 |
吸水率 | | | ASTM D570 |
23°C, 24 hr | 0.15 | % | |
平衡, 23°C, 50% RH | 0.32 | % | |
洛氏硬度 | | | ASTM D785 |
M 级 | 74 | | |
R 级 | 118 | | |
拉伸模量 | 2410 | MPa | ASTM D638 |
抗张强度 | | | ASTM D638 |
屈服 | 60.0 | MPa | |
断裂 | 72.0 | MPa | |
伸长率 | | | ASTM D638 |
屈服 | 6.0 | % | |
断裂 | 150 | % | |
弯曲模量 | 2410 | MPa | ASTM D790 |
弯曲强度 | 96.0 | MPa | ASTM D790 |
耐磨耗性 -
Change in Haze
2 | 45 | % | ASTM D1004 |
悬壁梁缺口冲击强度 (23°C) | 950 | J/m | ASTM D256 |
无缺口悬臂梁冲击 (23°C) | 无断裂 | | ASTM D256 |
装有测量仪表的落镖冲击 (23°C, Total Energy) | 94.0 | J | ASTM D3763 |
载荷下热变形温度 | | | ASTM D648 |
0.45 MPa, 退火,
4.00 mm | 146 | °C | |
1.8 MPa, 未退火,
4.00 mm | 132 | °C | |
1.8 MPa, 退火,
4.00 mm | 143 | °C | |
维卡软化温度 | 151 | °C | ASTM D1525 3 |
球压温度 | > 125 | °C | IEC 60598-1 |
线形热膨胀系数 -
流动
(-40 到 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
体积电阻率 (23°C) | 2.0E+17 | ohm
·cm | ASTM D257 |
介电强度 | 17 | kV/mm | ASTM D149 |
介电常数 (60 Hz) | 3.00 | | ASTM D150 |
耗散因数 (60 Hz) | 1.0E-3 | | ASTM D150 |
漏电起痕指数 (2.00 mm) | 250 | V | IEC 60112 |
热灯丝点火温度 4 (2.00 mm) | 850 | °C | IEC 60695-2-13 |
极限氧指数 | 26 | % | ASTM D2863 |
平均燃烧程度 | 3 | cm | ASTM D635 |
折射率 | 1.586 | | ASTM D542 |
透射率 | 89.0 | % | ASTM D1003 |
雾度 | 0.70 到
1.5 | % | ASTM D1003 |