供应耐高温PA9T/日本可乐丽/G1300H/增强30%GF/增强级PA9T
'
比重 | 1.37 | g/cm³ | No Standard |
熔流率 (320°C/2.16 kg) | 45 | g/10 min | ASTM D1238 |
收缩率 | | | No Standard |
流动 :
1.00 mm | 0.20 | % | |
横向流动 :
1.00 mm | 0.80 | % | |
吸水率 3 (饱和, 40°C) | 1.6 | % | No Standard |
抗张强度 | 160 | MPa | ASTM D638 |
伸长率 (断裂) | 4.0 | % | ASTM D638 |
弯曲模量 | 8500 | MPa | ASTM D790 |
弯曲强度 | 205 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 | 110 | J/m | ASTM D256 |
热变形温度 (1.8 MPa, 未退火) | 290 | °C | ASTM D648 |
玻璃转化温度(DSC) | 125 | °C | No Standard |
熔融温度 | 306 | °C | |
体积电阻率 | 1.0E+16 | ohm·cm | ASTM D257 |
介电强度 | 30 | kV/mm | ASTM D149 |
相对电容率 (10.0 GHz) | 3.30 | | ASTM D150 |
耗散因数 (10.0 GHz) | 0.0090 | | ASTM D150 |
相比耐漏电起痕指数(CTI) | PLC 0 | | UL 746 |
UL 阻燃等级 | HB | | UL 94 |
Bar Flow Length 4 (320°C, 500.0 µm) | 5.30 | cm | |
Weld Elongation | 0.60 | % | ASTM D638 |
Weld Strength | 45.0 | MPa | ASTM D638 |
'