供应PMMA/日本三菱丽阳/IR-H70/高抗冲PMMA/光学级PMMA/高透明
'
比重 | 1.14 | g/cm³ | ASTM D792 |
熔流率 (230°C/3.8 kg) | 0.70 | g/10 min | ASTM D1238 |
收缩率 - 流动 | 0.40 到 0.80 | % | ASTM D955 |
吸水率 (24 hr) | 0.40 | % | ASTM D570 |
洛氏硬度 (M 计秤) | 37 | | ASTM D785 |
抗张强度 2 | 32.4 | MPa | ASTM D638 |
伸长率 2 (断裂) | 90 | % | ASTM D638 |
弯曲模量 (6.35 mm) | 1280 | MPa | ASTM D790 |
弯曲强度 (6.35 mm) | 44.8 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 (6.35 mm) | 69 | J/m | ASTM D256 |
热变形温度 (1.8 MPa, 未退火) | 90.0 | °C | ASTM D648 |
维卡软化温度 | 105 | °C | ASTM D1525 |
线形膨胀系数 - 流动 | 0.00012 | cm/cm/°C | ASTM D696 |
折射率 | 1.490 | | ASTM D542 |
透射率 (3200 µm) | 92.0 | % | ASTM D1003 |
'