PMMA/韩国LG/HI835H/橡胶抗冲改性PMMA/超高韧性PMMA
'
比重 | 1.17 | g/cm³ | ASTM D792 |
熔流率 (230°C/3.8 kg) | 2.0 | g/10 min | ASTM D1238 |
收缩率 - 流动 | 0.40 到 0.80 | % | ASTM D955 |
吸水率 (24 hr) | 0.40 | % | ASTM D570 |
洛氏硬度 (M 计秤) | 57 | | ASTM D785 |
抗张强度 (屈服) | 43.1 | MPa | ASTM D638 |
伸长率 (屈服) | 100 | % | ASTM D638 |
弯曲模量 | 1740 | MPa | ASTM D790 |
弯曲强度 (屈服) | 79.4 | MPa | ASTM D790 |
简支梁缺口冲击强度 | 5.0 | kJ/m² | ISO 179/1eA |
简支梁缺口冲击强度 | 55 | kJ/m² | ISO 179/1eU |
悬壁梁缺口冲击强度 | 4.80 | kJ/m² | ASTM D256 |
热变形温度 (1.8 MPa, 未退火) | 83.0 | °C | ASTM D648 |
维卡软化温度 | 97.0 | °C | ASTM D1525 3 |
线形膨胀系数 - 流动 | 0.000070 | cm/cm/°C | ASTM D696 |
体积电阻率 | >
1.0E+15 | ohm·cm | ASTM D257 |
介电强度 4 | 15 | kV/mm | ASTM D149 |
介电常数 (60 Hz) | 3.10 | | ASTM D150 |
耗散因数 (60 Hz) | 0.040 | | ASTM D150 |
UL 阻燃等级 | HB | | UL 94 |
折射率 | 1.490 | | ASTM D542 |
透射率 (3200 µm) | 88.0 | % | ASTM D1003 |
雾度 (3200 µm) | <
1.5 | % | ASTM D1003 |
'