| 性能项目试验条件[状态]测试方法测试数据数据单位 |
| 基本性能吸水率JIS K-72090.3吸水率 |
| 物理性能全光透过率JIS K-710593% |
| 折射率JIS K-71051.49 |
| 流动系数JIS K-72102g/10min |
| 模糊度JIS K-71050.5% |
| 比重JIS K-71121.19 |
| 成形收缩率ASTM D-9550.2-0.6% |
| 机械性能抗冲击力JIS K-71101.7(1.7)Mpa(kgf/mm2) |
| 引张延伸率JIS K-711313% |
| 引张强度JIS K-711372.0(7.35)Mpa(kgf/mm2) |
| 杨氏模量弹性率JIS K-72033200(327)Mpa(kgf/mm2) |
| 弯曲强度JIS K-7203120(12.2)Mpa(kgf/mm2) |
| 硬度JIS K-7202100Mscale |
| 抗弯强刚度JIS K-72037% |
| 电气性能诱电正接JIS K-69110.04 |
| 绝缘抵抗JIS K-69111015Ω |
| 表面固有抵抗率JIS K-6911>1016Ω |
| 耐电压JIS K-691120KV/mm |
| 诱电率JIS K-69113.1 |
| 体积固有抵抗率JIS K-6911>1015Ω.cm |
| 热性能线膨胀系数JIS K-71977×10-5cm/cm/°C |
| 燃烧率JIS K-69113cm/min |
| 荷重热变形温度JIS K-7207104°C |
| 维卡软化点JIS K-7206116°C |