| VALOX ™ Resin 364 | SI | | British | | Metric | | PDF | Americas: COMMERCIAL |
| | | Designed for outdoor telecommunications enclosure applications. | | |
| TYPICAL PROPERTIES (1) | | MECHANICAL | Value | Unit | Standard | | Tensile Stress, yld, Type I, 50 mm/min | 470 | kgf/cm² | ASTM D 638 | | Tensile Stress, brk, Type I, 50 mm/min | 400 | kgf/cm² | ASTM D 638 | | Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 | | Tensile Strain, brk, Type I, 50 mm/min | 70 | % | ASTM D 638 | | Flexural Stress, yld, 1.3 mm/min, 50 mm span | 680 | kgf/cm² | ASTM D 790 | | Flexural Modulus, 1.3 mm/min, 50 mm span | 18900 | kgf/cm² | ASTM D 790 | | IMPACT | Value | Unit | Standard | | Izod Impact, notched, 23°C | 76 | cm-kgf/cm | ASTM D 256 | | Izod Impact, notched, -20°C | 70 | cm-kgf/cm | ASTM D 256 | | Izod Impact, notched, -40°C | 43 | cm-kgf/cm | ASTM D 256 | | Instrumented Impact Total Energy, 23°C | 460 | cm-kgf | ASTM D 3763 | | Instrumented Impact Total Energy, -20°C | 456 | cm-kgf | ASTM D 3763 | | Instrumented Impact Total Energy, -40°C | 483 | cm-kgf | ASTM D 3763 | | THERMAL | Value | Unit | Standard | | Vicat Softening Temp, Rate B/50 | 115 | °C | ASTM D 1525 | | HDT, 0.45 MPa, 3.2 mm, unannealed | 103 | °C | ASTM D 648 | | HDT, 1.82 MPa, 3.2mm, unannealed | 68 | °C | ASTM D 648 | | CTE, -40°C to 40°C, flow | 9.5E-05 | 1/°C | ASTM E 831 | | CTE, -40°C to 40°C, xflow | 9.8E-05 | 1/°C | ASTM E 831 | | CTE, -40°C to 40°C, flow | 9.5E-05 | 1/°C | ISO 11359-2 | | CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 | | Vicat Softening Temp, Rate B/120 | 122 | °C | ISO 306 | | Relative Temp Index, Elec | 75 | °C | UL 746B | | Relative Temp Index, Mech w/impact | 75 | °C | UL 746B | | Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B | | PHYSICAL | Value | Unit | Standard | | Specific Gravity | 1.3 | - | ASTM D 792 | | Mold Shrinkage, flow, 3.2 mm (5) | 0.8 - 1 | % | SABIC Method | | Mold Shrinkage, xflow, 3.2 mm (5) | 0.8 - 1 | % | SABIC Method | | ELECTRICAL | Value | Unit | Standard | | Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | | Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | | High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A | | High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | | Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | | FLAME CHARACTERISTICS | Value | Unit | Standard | | UL Recognized, 94V-0 Flame Class Rating (3) | 1.47 | mm | UL 94 | | UL Recognized, 94-5VA Rating (3) | 2.99 | mm | UL 94 | | Oxygen Index (LOI) | 28 | % | ASTM D 2863 | | UV-light, water exposure/immersion | F2 | - | UL 746C |
| Source GMD, last updated:2000/08/01 |
| Parameter | | Injection Molding | Value | Unit | | Drying Temperature | 120 | °C | | Drying Time | 3 - 4 | hrs | | Drying Time (Cumulative) | 12 | hrs | | Maximum Moisture Content | 0.02 | % | | Melt Temperature | 250 - 265 | °C | | Nozzle Temperature | 245 - 260 | °C | | Front - Zone 3 Temperature | 250 - 265 | °C | | Middle - Zone 2 Temperature | 245 - 260 | °C | | Rear - Zone 1 Temperature | 240 - 255 | °C | | Mold Temperature | 50 - 75 | °C | | Back Pressure | 0.3 - 0.7 | MPa | | Screw Speed | 50 - 100 | rpm | | Shot to Cylinder Size | 40 - 80 | % | | Vent Depth | 0.025 - 0.038 | mm |
| Source GMD, last updated:2000/08/01 |
|