| XENOY ™ Resin 1760 | SI | | British | | Metric | | PDF | Americas: COMMERCIAL |
| | | 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. | | |
| TYPICAL PROPERTIES (1) | | MECHANICAL | Value | Unit | Standard | | Tensile Stress, yld, Type I, 5 mm/min | 850 | kgf/cm² | ASTM D 638 | | Tensile Stress, brk, Type I, 5 mm/min | 850 | kgf/cm² | ASTM D 638 | | Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | | Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D 638 | | Tensile Modulus, 5 mm/min | 54200 | kgf/cm² | ASTM D 638 | | Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1330 | kgf/cm² | ASTM D 790 | | Flexural Modulus, 1.3 mm/min, 50 mm span | 39800 | kgf/cm² | ASTM D 790 | | Tensile Stress, yield, 5 mm/min | 84 | MPa | ISO 527 | | Tensile Stress, break, 5 mm/min | 84 | MPa | ISO 527 | | Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | | Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | | Tensile Modulus, 1 mm/min | 4950 | MPa | ISO 527 | | Flexural Stress, yield, 2 mm/min | 134 | MPa | ISO 178 | | Flexural Modulus, 2 mm/min | 4050 | MPa | ISO 178 | | IMPACT | Value | Unit | Standard | | Izod Impact, notched, 23°C | 9 | cm-kgf/cm | ASTM D 256 | | Izod Impact, notched, -30°C | 8 | cm-kgf/cm | ASTM D 256 | | Instrumented Impact, Energy @ peak, -20°C | 40 | cm-kgf | ASTM D 3763 | | Instrumented Impact Energy @ peak, -30 | 30 | cm-kgf | ASTM D 3763 | | Instrumented Impact Total Energy, 23°C | 81 | cm-kgf | ASTM D 3763 | | Instrumented Impact Total Energy, -30°C | 30 | cm-kgf | ASTM D 3763 | | Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A | | Izod Impact, notched 80*10*4 -30°C | 3 | kJ/m² | ISO 180/1A | | Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 16 | kJ/m² | ISO 179/1eA | | THERMAL | Value | Unit | Standard | | Vicat Softening Temp, Rate B/50 | 121 | °C | ASTM D 1525 | | HDT, 1.82 MPa, 6.4 mm, unannealed | 115 | °C | ASTM D 648 | | CTE, -40°C to 40°C, flow | 7.7E-05 | 1/°C | ASTM E 831 | | CTE, -40°C to 40°C, xflow | 3.8E-05 | 1/°C | ASTM E 831 | | CTE, -40°C to 95°C, flow | 4.5E-05 | 1/°C | ASTM E 831 | | CTE, -40°C to 95°C, xflow | 7.38E-05 | 1/°C | ASTM E 831 | | CTE, -40°C to 40°C, flow | 7.7E-05 | 1/°C | ISO 11359-2 | | CTE, -40°C to 40°C, xflow | 3.8E-05 | 1/°C | ISO 11359-2 | | Vicat Softening Temp, Rate B/50 | 135 | °C | ISO 306 | | Vicat Softening Temp, Rate B/120 | 130 | °C | ISO 306 | | HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 104 | °C | ISO 75/Af | | PHYSICAL | Value | Unit | Standard | | Specific Gravity | 1.3 | - | ASTM D 792 | | Mold Shrinkage, flow, 3.2 mm (5) | 0.4 - 0.6 | % | SABIC Method | | Mold Shrinkage, xflow, 3.2 mm (5) | 0.4 - 0.6 | % | SABIC Method | | Density | 1.3 | g/cm³ | ISO 1183 | | Water Absorption, (23°C/sat) | 0.5 | % | ISO 62 | | Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 | | Melt Volume Rate, MVR at 265°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:2011/02/04 |
| Parameter | | Injection Molding | Value | Unit | | Drying Temperature | 110 | °C | | Drying Time | 4 - 6 | hrs | | Drying Time (Cumulative) | 8 | hrs | | Maximum Moisture Content | 0.02 | % | | Melt Temperature | 260 - 280 | °C | | Nozzle Temperature | 255 - 275 | °C | | Front - Zone 3 Temperature | 260 - 280 | °C | | Middle - Zone 2 Temperature | 255 - 275 | °C | | Rear - Zone 1 Temperature | 250 - 270 | °C | | Mold Temperature | 65 - 95 | °C | | Back Pressure | 0.3 - 0.6 | MPa | | Screw Speed | 50 - 80 | rpm | | Shot to Cylinder Size | 50 - 80 | % | | Vent Depth | 0.013 - 0.02 | mm |
| Source GMD, last updated:2011/02/04 |
|
|