沙伯基础创新塑料 PC+PET XENOY 2230
中山沙泊塑料(东莞)有限公司
中国 东莞
产品属性
图文详情
品牌推荐
品牌/厂家
沙伯基础创新塑料
牌号
2230
类型
正牌料
产地
美国
熔体流动速率
3.6g/10min
密度
1.22g/cm3
拉伸强度
65kg/cm2
弯曲强度
32kg/cm2
弯曲模量
54kg/cm2
缺口冲击强度
67kg.cm/cm
断裂伸长率
0.82%
成型收缩率
0.6 - 0.9%
洛氏硬度
110HR
热变形温度
129℃
脆化温度
145℃
维卡软化点
280°F
沙伯基础创新塑料 PC+PET XENOY 2230 无筋、不透明的聚碳酸酯基聚合物合金。提供耐化学性、尺寸稳定性和机械性能。
| XENOY ™ Resin 2230 | SI | | British | | Metric | Americas: COMMERCIAL |
| Unreinforced, opaque, polycarbonate-based polymer alloy. Offers chemical resistance, dimensional stability and mechanical performance. |
| Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min | 560 | kgf/cm² | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 120 | % | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 870 | kgf/cm² | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 22800 | kgf/cm² | ASTM D 790 | |
| Hardness, Rockwell R | 115 | - | ASTM D 785 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 81 | cm-kgf/cm | ASTM D 256 | |
| Gardner, 23°C | 553 | cm-kgf | ASTM D 3029 | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 129 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 121 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 5.4E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 6.12E-05 | 1/°C | ASTM E 831 | |
| Relative Temp Index, Elec | 75 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.22 | - | ASTM D 792 | |
| Specific Volume | 0.82 | cm³/g | ASTM D 792 | |
| Water Absorption, 24 hours | 0.14 | % | ASTM D 570 | |
| Water Absorption, equilibrium, 23C | 0.6 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.6 - 0.9 | % | SABIC Method | |
| Mold Shrinkage on Tensile Bar, xflow (2) (5) | 0.6 - 0.9 | % | SABIC Method | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | 2.1E+16 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in air, 3.2 mm | 21.2 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 100 Hz | 3.6 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 3.2 | - | ASTM D 150 | |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.005 | - | ASTM D 150 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) | 0.81 | mm | UL 94 | |
| Source GMD, last updated:2014/01/03 |
| Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 280 | °C |
| Nozzle Temperature | 255 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 255 - 275 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Mold Temperature | 65 - 95 | °C |
| Back Pressure | 0.3 - 0.6 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 50 - 80 | % |
| Vent Depth | 0.013 - 0.02 | mm |