东莞市常平来万特塑胶原料经营部

CYCOLAC*ABS:
AES145,AES145UV,AP95,AS200GF,AS35,AS35UV,
BDT5510,BDT6500,CRT3370,CRT3370F,CTR52,CTR52F
,DL100,EX39,EX39F,EX58,EX58F,EXABS01,FR15,
FR15U,FR23,FR30U,FXS600ARM,FXS610AR,
FXS610SK,FXS610SP,FXS610ST,FXS612SK,
FXS650SK,FXS680GL,FXS680SK,G121,G122
,G151,G320,G360,G361,G362,G363,G365,G366
,G368,GDT2510,GDT5500L,GDT6400,GDT6832L,
GDT6804L,GHT3330,GHT3510,GHT3511,GHT3512
,GHT4320,GHT4400,GPB3800,GLB2960.GPM4700.
GPM4700P,GPM5500,GPM5500F,GPM5500S,
GPM5500U,GPM5600T,GPM7300.GPM6300.
GPT5500.GPT3800,GPT4600,GPP4600,GPP4500,
GPP4800,GPP3900,GPX3700,GPX3800,GPX2800,
GKX4500,GX3800F,HMG47MD,HMG94MD,HP20,
HP30,MG29,MG34LG,MG34LGHF,MG37CR,
MG37EP,MG37EPN,MG38,MG38F,MG38N,MG47
,MG47F,MG47MD,MG47N,MG47TG,MG8000SR,
MG94,MG94MD,MG94U,MGABS01,MGABS02,
MGX53GP,MGX620ST,REC550,S157,S570,S700,
S700S,S700T,S701,S701S,S702,S702S,S702U,
S703,S703S,S703T,S704,S704S,S705,S706S,
S708C,S848,S850,S858,SEA2,SEA2X,V100,VW300,
VW55,X11,X11G,X15,X15G,X17,X37,Z48.LDM,LDA,
CGA,LSA,LS,GSE,EP,ETC,EPBM,AR,T,L,KJB,KJU
,KJW,GKX,GPB,GLB,
产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
熔体流动速率 | 230℃/3.8kg | ASTM D-1238 | 3.3 | g/10min |
比重 | | ASTM D-792 | 1.19 | g/cm3 |
模具收缩率 | Flow 3.20mm | ASTM D-955 | 0.50-0.70 | % |
拉伸模量 | | ASTM D-638 | 2070 | MPa |
拉伸屈服强度 | | ASTM D-638 | 37.8 | MPa |
拉伸断裂强度 | | ASTM D-638 | 30.3 | MPa |
拉伸屈服伸长率 | | ASTM D-638 | 2.4 | % |
拉伸断裂伸长率 | | ASTM D-638 | 17 | % |
弯曲模量 | 50.0mm Span | ASTM D-790 | 2340 | MPa |
弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 67.6 | MPa |
IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 214 | J/m |
体积电阻率 | | IEC 60093 | >1.0E+14 | ohm.cm |
介电强度 | 3.20mm in Oil | IEC 60243-1 | 20.00 | KV/mm |
热变形温度 | 0.45MPa,未退火,3.20mm | ASTM D-648 | 86.1 | ℃ |
热变形温度 | 1.80MPa,未退火,3.20mm | ASTM D-648 | 75.0 | ℃ |
维卡软化温度 | | ASTM D-1525 | 93.9 | ℃ |
CLTE | Flow -40TO40℃ | ASTM E-831 | 0.000090 | cm/cm/℃ |
CLTE | Transverse -40TO40℃ | ASTM E-831 | 0.000092 | cm/cm/℃ |
燃烧性 | 1.50mm | UL 94 | V-0 |
燃烧性 | 2.79mm | UL 94 | 5VA |