LLDPE的流变性可概括为"剪切时刚性"和"延伸时柔软"。 当用LLDPE替代LDPE时薄膜挤塑设备和条件必须做修改。
原料描述部分
|
规格级别 |
其它 薄膜 吹塑 |
外观颜色 |
|
|
该料用途 |
各类购物袋、轻中包装膜、超薄膜、伸缩膜。 |
|
备注说明 |
特性：热封性佳、薄膜延伸性佳、押出性佳、3224开口中等、3224D开口佳。 |
原料技术数据
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
基本性能 |
熔体流动速率 |
|
ASTM D-1238 |
2.0 |
g/10min |
|
密度 |
|
ASTM D-1505 |
0.920 |
g/cm3 |
|
机械性能 |
落球冲击强度 |
|
ASTM D-1709 |
120 |
g |
|
抗撕裂性 |
MD |
|
ASTM D-1922 |
40 |
g/25µm |
|
TD |
|
ASTM D-1922 |
430 |
g/25µm |
|
拉力断裂强度 |
MD |
|
ASTM D-882B |
360 |
Kg/cm2 |
|
TD |
|
ASTM D-882B |
280 |
Kg/cm2 |
|
拉力降伏强度 |
MD |
|
ASTM D-882B |
100 |
Kg/cm2 |
|
TD |
|
ASTM D-882B |
110 |
Kg/cm2 |
|
1%伸长弹性系数 |
MD |
|
ASTM D-882B |
1500 |
Kg/cm2 |
|
TD |
|
ASTM D-882B |
2100 |
Kg/cm2 |
|
拉力断裂伸长率 |
MD |
|
ASTM D-882B |
600 |
% |
|
TD |
|
ASTM D-882B |
800 |
% |
|
热性能 |
脆化温度 |
|
ASTM D-746 |
<-70 |
℃ |
|
熔点 |
|
DSC |
122 |
℃ |
|
软化点 |
|
ASTM D-1525 |
93 |
℃ |
|
其它性能 |
开口剂 |
|
|
中 |
|
|
滑剂 |
|
|
中 |
|
|
浊度 |
|
ASTM D-1003 |
22 |
% |