ABS 台湾奇美 PA-758R 吸尘器外壳 PA758R 3C产品外壳 文具制品用

MABS POLYLAC® Characteristics PA-758R
特性
PROPERTIES
測試方法
ASTM
TEST METHOD
測試條件
TEST CONDITION
單位
UNIT
一般級 GENERAL
PA-758R
熔融指數
Melt Flow Index D1238 22 20 00℃ ℃,,10 5 Kg Kg g/10 min 2.2 -
比重
Mass Density D792 23 ℃ - 1.08
硬度
Hardness D785 - R Scale 110
拉伸強度 (屈服)
Tensile Strength (Yield) D638 6 mm/min Kg/cm lb/in2 2 572 420 0
延伸率
Tensile Elongation D638 6 mm/min % 65
彎曲強度
Flexural Strength D790 2.8 mm/min
Kg/cm2 610
lb/in2 8650
彎曲彈性模數
Flexural Modulus D790 2.8 mm/min 10 10 4 5Kg/cm lb/in2 2 2.1 3.0
IZOD 衝擊強度
Izod Impact Strength D256 (Notched)
6.4 mm, 23℃
Kg-cm/cm 16
ft-lb/in 3.0
3.2 mm, 23℃
Kg-cm/cm 15
ft-lb/in 2.8
維氏軟化溫度
Vicat Softening Temp. D1525 1 Kg,50 ℃/hr
℃ 102
℉ 216
熱變形溫度
Heat Distortion Temp. D648
1.8 MPa Annealed
℃ 97
℉ 207
1.8 MPa
Unannealed
℃ 86
℉ 187
UL 燃燒等級
UL Flammability UL 94 - - 1.5 mm HB
December 19, 2013
Notes：These are typical properties only and are not to be construed as specifications. Users should confirm
results by their own tests.