长期供应PC/ABS沙伯基础1200-701 阻燃
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | | 物理性能 | 比重 | --- | ASTN D-792 | 1.15 | --- | | 吸水率 | --- | ASTM D-570 | - | % | | 模具收缩率 | 3.2mm | ASTM D-955 | 5-7 | E-3 | | 机械性能 | 拉伸强度(屈伏点) | --- | ASTM D-638 | 57 | Mpa | | 拉伸率(断裂点) | --- | ASTM D-638 | 150 | % | | 拉伸模量 | --- | ASTM D-638 | 2247 | Mpa | | 弯曲强度 | --- | ASTM D-790 | 88 | Mpa | | 弯曲模量 | --- | ASTM D-790 | 2343 | Mpa | | 冲击强度缺口 | 23℃ | ASTM D-256 | 587 | J/m | | 洛氏硬度 | --- | ASTM D-785 | - | R | | 电气性能 | 损耗因数 | 1MHz | ASTM D-150 | - | --- | | 介电常数 | 1MHz | ASTM D-150 | - | --- | | 体积电阻 | --- | ASTM D-257 | - | Ohm-cm | | 表面电阻 | --- | ASTM D-257 | - | Ohm-cm | | 热 性 能 | 阻燃性 | --- | UL-94 | - | --- | | 阻燃性 | --- | UL-94 | - | mm | | 热变形温度 | 0.45Mpa | ASTM D-648 | 129 | ℃ | | 热变形温度 | 1.8Mpa | ASTM D-648 | 112 | ℃ | | 维卡软化点 | --- | ASTM D-1525 | - | ℃ | | 线膨胀系数 | --- | ASTM E831 | 7.2E-05 | 1/℃ | | UL长期使用温度 | 含冲击 | UL-746B | - | ℃ | | UL长期使用温度 | 无冲击 | UL-746B | -
|
|
|