Eastman is pleased to announce the launch of DRYSTAR* copolyesters. This new product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman?s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment.
Recognizing this value, Eastman conceived Drystar™ copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find Drystar™ copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of Drystar™ copolyesters and Eastman has on-going program to extend this strategic product-line in the future.
*DRYSTAR is only available in the Asia Pacific Region.
单位: 公制 | 英制
| 总体 | ||||
材料状态 |
| |||
资料 1 | ||||
搜索 UL 黄卡 |
| |||
供货地区 |
| |||
特性 |
| |||
形式 |
| |||
加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
比重 | |||
-- | 1.27 |
| ASTM D792 |
73°F | 1.27 | g/cm³ | ISO 1183/D |
-- | 1.27 | g/cm³ | ASTM D1505 |
吸水率 (73°F, 24 hr) | 0.13 | % | ASTM D570, ISO 62 |
固有粘度 2 | 内部方法 | ||
Film : 73°F | 0.70 |
| |
Pellets : 73°F | 0.75 |
| |
| 硬度 | 额定值 | 单位制 | 测试方法 |
洛氏硬度 | |||
R 级, 73°F | 106 |
| ASTM D785 |
R 计秤, 73°F | 109 |
| ISO 2039-2 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 (73°F) | 305000 | psi | ASTM D638, ISO 527-2 |
抗张强度 | ASTM D638, ISO 527-2 | ||
屈服, 73°F | 7250 | psi | |
断裂, 73°F | 4060 | psi | |
伸长率 | |||
断裂, 73°F | 130 | % | ASTM D638 |
断裂, 73°F | 100 | % | ISO 527-2 |
弯曲模量 | |||
73°F | 305000 | psi | ASTM D790 |
73°F | 290000 | psi | ISO 178 |
弯曲应力 | |||
73°F | 9860 | psi | ISO 178 |
屈服, 73°F | 10200 | psi | ASTM D790 |
撕裂阻力 | ASTM D2582 | ||
M.D. : 73°F | 93 | N | |
T.D. : 73°F | 93 | N | |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
薄膜厚度 - 经测试 | 9.8 | mil | |
割线模量 | ASTM D882 | ||
MD | 276000 | psi | |
TD | 276000 | psi | |
抗张强度 | ASTM D882 | ||
MD : 屈服 | 7540 | psi | |
TD : 屈服 | 7540 | psi | |
MD : 断裂 | 8560 | psi | |
TD : 断裂 | 7980 | psi | |
伸长率 | ASTM D882 | ||
MD : 屈服 | 4.0 | % | |
TD : 屈服 | 4.0 | % | |
MD : 断裂 | 400 | % | |
TD : 断裂 | 400 | % | |
落锤冲击 3 | ASTM D1709A | ||
0°F | 500 | g | |
73°F | 400 | g | |
埃尔曼多夫抗撕强度 | ASTM D1922 | ||
MD | 1400 | g | |
TD | 1700 | g | |
裤型撕裂耐性 4 | ISO 6383-1 | ||
MD | 206 | lbf/in | |
TD | 206 | lbf/in | |
透氧率 (73°F) | 25 | cm³·mil/100in²/atm/24 hr | ASTM D3985 |
水气透过率 (100°F, 100% RH) | 0.45 | g/100 in²/24 hr | ASTM F1249 |
Carbon Dioxide Permeability 5 (73°F) | 120 | cm³·mil/100in²/atm/24 hr | ASTM D1434 |
抗撕裂蔓延性 6 | ASTM D1938 | ||
M.D. : 73°F | 210 | lbf/in | |
T.D. : 73°F | 210 | lbf/in | |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
悬壁梁缺口冲击强度 | |||
-40°F | 0.69 | ft·lb/in | ASTM D256 |
73°F | 1.9 | ft·lb/in | ASTM D256 |
-40°F | 2.0 | ft·lb/in² | ISO 180/1A |
73°F | 3.0 | ft·lb/in² | ISO 180/1A |
无缺口悬臂梁冲击 | |||
-40°F, 0.126 in | 无断裂 |
| ASTM D4812 |
-22°F, 0.126 in | 无断裂 |
| ASTM D4812 |
-4°F, 0.126 in | 无断裂 |
| ASTM D4812 |
73°F, 0.126 in | 无断裂 |
| ASTM D4812 |
-40°F 7 | 无断裂 |
| ISO 180/1U |
-22°F 7 | 无断裂 |
| ISO 180/1U |
-4°F 7 | 无断裂 |
| ISO 180/1U |
73°F 7 | 无断裂 |
| ISO 180/1U |
装有测量仪表的落镖冲击 | |||
-40°F, 0.0984 in, Energy at Peak Load | 363 | in·lb | ASTM D3763 |
-40°F, 0.126 in, Energy at Peak Load | 443 | in·lb | ASTM D3763 |
73°F, 0.0984 in, Energy at Peak Load | 248 | in·lb | ASTM D3763 |
73°F, 0.126 in, Energy at Peak Load | 292 | in·lb | ASTM D3763 |
-40°F, 0.0984 in, 能量到力量峰值 8, 9 | 25.8 | ft·lb | ISO 6603-2 |
-40°F, 0.126 in, 能量到力量峰值 8, 9 | 26.6 | ft·lb | ISO 6603-2 |
73°F, 0.0984 in, 能量到力量峰值 8, 9 | 29.5 | ft·lb | ISO 6603-2 |
73°F, 0.126 in, 能量到力量峰值 8, 9 | 32.5 | ft·lb | ISO 6603-2 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
载荷下热变形温度 | ASTM D648 | ||
66 psi, 未退火 | 158 | °F | |
264 psi, 未退火 | 147 | °F | |
玻璃转化温度 | 176 | °F | DSC |
维卡软化温度 | 185 | °F | ASTM D1525 |
线形热膨胀系数 - 流动 (-22 到 104°F) | 2.8E-5 | in/in/°F | ASTM D696 |
比热 | DSC | ||
140°F | 0.311 | Btu/lb/°F | |
212°F | 0.421 | Btu/lb/°F | |
302°F | 0.449 | Btu/lb/°F | |
392°F | 0.471 | Btu/lb/°F | |
482°F | 0.490 | Btu/lb/°F | |
导热系数 (73°F) | 1.5 | Btu·in/hr/ft²/°F | ASTM C177 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
表面电阻率 | 1.0E+16 | ohms | ASTM D257 |
体积电阻率 (73°F) | 1.0E+15 | ohms·cm | ASTM D257 |
介电强度 10 (73°F) | 410 | V/mil | ASTM D149 |
介电常数 | ASTM D150 | ||
73°F, 1 kHz | 2.60 |
| |
73°F, 1 MHz | 2.40 |
| |
耗散因数 | ASTM D150 | ||
73°F, 1 kHz | 5.0E-3 |
| |
73°F, 1 MHz | 0.020 |
| |
耐电弧性 | 158 | sec | ASTM D495 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
光泽度 (45°) | 108 |
| ASTM D2457 |
透射率 | ASTM D1003 | ||
常规 | 89.0 | % | |
总计 | 91.0 | % | |
透明度 | 85.0 |
| ASTM D1746 |
雾度 | 0.80 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 |
|
干燥温度 | 158 | °F | |
干燥时间 | 6.0 | hr | |
加工（熔体）温度 | 482 到 518 | °F | |
模具温度 | 59 到 104 | °F |