PC/日本帝人/L-1225Z100汽车部件光学级电子部件抗紫外线
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 密度 | | ASTM D-792 | 1200 | kg/m3 |
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.15 | % |
| 平衡吸水率 | 23℃,相对湿度50% | ASTM D-570 | 0.32 | % |
| 熔体流动速率 | | ASTM D-1238 | 10 | g/10min |
| 物理性能 | 比重 | | ASTM D-792 | 1.20 | |
| 折射率 | | ASTM D-542 | 1.586 | |
| 模具收缩率 | | ASTM D-955 | 0.005-0.007 | mm/mm |
| 透光率 | | ASTM D-1003 | 89 | % |
| 雾度 | | ASTM D-1003 | 0.7-1.5 | % |
| 机械性能 | 缺口冲击强度 | 23℃ | ASTM D-256 | 900 | J/m |
| 冲击强度 | 23℃ | ASTM D-256 | 未破裂 | |
| 洛氏硬度 | | ASTM D-785 | 73 | M标度 |
| 拉伸强度 | 屈服点 | | ASTM D-638 | 60 | MPa |
| 断裂点 | | ASTM D-638 | 71 | MPa |
| 弯曲强度 | | ASTM D-790 | 96 | MPa |
| 拉伸模量 | | ASTM D-638 | 2410 | MPa |
| 弯曲模量 | | ASTM D-790 | 2410 | MPa |
| 伸长率 | 屈服点 | | ASTM D-638 | 60 | % |
| 断裂点 | | ASTM D-638 | 150 | % |
| 落锤冲击强度 | 23℃ | ASTM D-3763 | 87 | J |
| 电气性能 | 介电强度 | 60HZ | ASTM D-149 | 17 | kv/mm |
| 对比电弧径迹指数 | 2mm | IEC 112 | 250 | v |
| 辉光灯丝测试 | 2mm | IEC 695-2-1 | 850 | ℃ |
| 损耗因素 | 60Hz | ASTM D-150 | 0.001 | |
| 体积电阻率 | 23℃,干 | ASTM D-257 | 2.0×1017 | Ω.cm |
| 热性能 | 热变形温度 | 退火@0.45MPa(4 mm) | ASTM D-648 | 144 | ℃ |
| 热变形温度 | 退火@1.82MPa(4 mm) | ASTM D-648 | 141 | ℃ |
| 球状压良温度 | | IEC 598-1 | >125 | ℃ |
| 线性热收缩率 | -40℃-82℃ | ASTM D-696 | 68×10-6 | mm/mm/℃ |
| 平均燃烧程度 | | ASTM D-635 | 25 | mm |
| 热变形温度 | 未退火@1.82MPa(4 mm) | ASTM D-648 | 128 | ℃ |
| 维卡软化点 | 50 C/hour | ASTM D-1525 | 149 | ℃ |
| 其它性能 | 需氧系数 | | ASTM D-2863 | 26 | % |
| 阻燃性 | 1.5mm | UL 94 | V-2 | |
| 1.6mm | UL 94 | V-2 | |
| 2.5-2.7mm | UL 94 | V-2 | |
| 3.0mm | UL 94 | HB | |