*PWHT 755°C 2h*
Elongation	Tensile Strength	Yield Strength	保护气体	Stress Relieved Temperature	Stress Relieved Testing Time
21 %	820 MPa	720 MPa	ISO	-	-
*Stress relieved*
Elongation	Tensile Strength	Yield Strength	保护气体	Stress Relieved Temperature	Stress Relieved Testing Time
-	-	-	ISO	760 °C	3 hr
*PWHT 755°C 2h*
Elongation	Tensile Strength	Yield Strength	保护气体	Stress Relieved Temperature	Stress Relieved Testing Time
-	-	-	AWS	-	-

*PWHT 755°C 2h*
Impact Value	Testing Temperature	保护气体	Stress Relieved Testing Temp	Stress Relieved Testing Time
50 J	20 °C	ISO	-	-
*Stress relieved*
Impact Value	Testing Temperature	保护气体	Stress Relieved Testing Temp	Stress Relieved Testing Time
-	20 °C	ISO	760 °C	3 hr

Fusion time per electrode at 90% I max	kg weld metal/kg electrodes	Number of electrodes/kg weld metal	安培	熔敷率	电压 V	直径
56 sec	0.66 kg	71.4	70-100 A	0.90 kg/h	21 V	2.5 x 350 mm
68 sec	0.60 kg	45.5	90-135 A	1.20 kg/h	22 V	3.2 x 350 mm
85 sec	0.64 kg	22.6	130-200 A	1.90 kg/h	23 V	4.0 x 450 mm