OK AristoRod™ 13.08是一种适用于抗蠕变钢GMAW焊接的0.4Mo合金化(ER80S-D2)实芯焊丝，该抗蠕变钢与500°C工作温度下使用材料的成分相同。AristoRod™ 13.08经过伊萨独有的先进表面特性(ASC)技术处理，其可将MAG焊接操作提升到全新高度，并且在机器人和自动化焊接中具有全方位的高效性。其特性包括优良的引弧性能；无故障高速送丝和远距离送丝；较高焊接电流下电弧极其稳定；飞溅少；较低烟尘排放；导电嘴磨损少且焊丝腐蚀防护得到改善。
Typical Tensile Properties
| AWS CO2 (C1) As welded |
| Elongation | Tensile Strength | Yield Strength |
| 25 % | 645 MPa | 540 MPa |
| EN 80Ar/20CO2 (M21) As welded |
| Elongation | Tensile Strength | Yield Strength |
| 24 % | 685 MPa | 590 MPa |
夏比V型缺口冲击性能| AWS CO2 (C1) As welded |
| Impact Value | Testing Temperature |
| 90 J | 20 °C |
| 36 J | -20 °C |
| - | -29 °C |
| 38 J | -40 °C |
| EN 80Ar/20CO2 (M21) As welded |
| Impact Value | Testing Temperature |
| 140 J | 20 °C |
| 100 J | -20 °C |
| 80 J | -40 °C |
焊缝金属分析| Mn |
| Mn | Mo | C | Si | Ni | Cr |
| 1.78 % | - | - | - | - | - |
| Mo |
| Mn | Mo | C | Si | Ni | Cr |
| - | 0.47 % | - | - | - | - |
| C |
| Mn | Mo | C | Si | Ni | Cr |
| - | - | 0.098 % | - | - | - |
| Si |
| Mn | Mo | C | Si | Ni | Cr |
| - | - | - | 0.6 % | - | - |
| Ni |
| Mn | Mo | C | Si | Ni | Cr |
| - | - | - | - | 0.05 % | - |
| Cr |
| Mn | Mo | C | Si | Ni | Cr |
| - | - | - | - | - | 0.04 % |
熔敷数据| 安培 | 熔敷率 | 电压 V | 直径 | 送丝速度 |
| 40-170 A | 0,4-2,6 kg/h | 16-22 V | 0.8 mm | 2-10,8 m/min |
| 70-280 A | 1-5,4 kg/h | 18-28 V | 0.9 mm | 2,7-14,7 m/min |
| 90-300 A | 1-5,4 kg/h | 18-28 V | 1.0 mm | 2,7-14,7 m/min |
| 120-350 A | 1,5-6,6 kg/h | 20-33 V | 1.2 mm | 2,7-12,4 m/min |
| 225-480 A | 3,3-11.6 kg/h | 26-38 V | 1.6 mm | 3,10-12 m/min |